POM KF006 BK SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive Applications
heat-resisting,high strength,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/KF006 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KF006 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9200 Mpa | |
| tensile strength | 屈服 | ISO 527-2/5 | 125 Mpa |
| bending strength | ISO 178 | 163 Mpa | |
| Flexural modulus | ISO 178 | 7400 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.9 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/KF006 BK |
|---|---|---|---|
| Shrinkage rate | 横向流动 | 内部方法 | 0.80 - 1.1 % |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.40 % |
| Shrinkage rate | 流动 | 内部方法 | 0.50 - 0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KF006 BK |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距，HDT | ISO 75-2/Bf | 164 °C |
| Linear coefficient of thermal expansion | 流动 : 23 到 60°C | ISO 11359-2 | 3.2E-5 cm/cm/°C |
| 横向 : 23 到 60°C | ISO 11359-2 | 9.6E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距，HDT | ISO 75-2/Af | 161 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/KF006 BK |
|---|---|---|---|
| drying time | 4.0 hr | ||
| screw speed | 30 to 60 rpm | ||
| Temperature in the middle of the barrel | 195 to 205 °C | ||
| Temperature at the rear of the barrel | 175 to 190 °C | ||
| Processing (melt) temperature | 200 to 215 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 210 to 220 °C | ||
| Back pressure | 0.200 to 0.300 Mpa | ||
| Temperature | 80 to 110 °C |