PC DFL4034 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical Applications
Easy to demould,Easy to form
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL4034 |
|---|---|---|---|
| 0.45MPa, unannealed, 3.20mm | ASTM D648 | 146 °C | |
| 0.45MPa, unannealed, 64.0mm span | ISO 75-2/Bf | 146 °C | |
| 1.8MPa, unannealed, 3.20mm | ASTM D648 | 142 °C | |
| 1.8MPa, unannealed, 64.0mm span of | ISO 75-2/Af | 141 °C | |
| Linear coefficient of thermal expansion | TD:-30到30°C | ASTM D696 | 6.3E-05 cm/cm/°C |
| MD:-30到30°C | ASTM D696 | 3.7E-05 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL4034 |
|---|---|---|---|
| --1 | ASTM D638 | 7190 Mpa | |
| --5 | ISO 178 | 6200 Mpa | |
| 50.0mm span | ASTM D790 | 6320 Mpa | |
| crack | ASTM D638 | 95.0 Mpa | |
| ISO 527-2/5 | 93.0 Mpa | ||
| ASTM D638 | 2.7 % | ||
| ISO 527-2/5 | 3.1 % | ||
| Fracture, 50.0mm span | ASTM D790 | 145 Mpa | |
| Friction coefficient | 与自身-动态 | ASTM D3702Modified | 0.46 |
| 与自身-静态 | ASTM D3702Modified | 0.50 | |
| Wear factor | Ring | ASTM D3702Modified | 13.0 10^-10in^5-min/ft-lb-hr |
| Washer | ASTM D3702Modified | 89.0 10^-10in^5-min/ft-lb-hr | |
| yield | ISO 527-2/5 | 2.8 % |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL4034 |
|---|---|---|---|
| 24hr,50%RH | ASTM D570 | 0.090 % | |
| Balance, 23 ° C, 50% RH | ISO 62 | 0.13 % | |
| Shrinkage rate | MD:24小时 | ASTM D955 | 0.020-0.040 % |
| TD:24小时 | ASTM D955 | 0.20-0.40 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL4034 |
|---|---|---|---|
| 23°C | ASTM D256 | 150 J/m | |
| ASTM D4812 | 740 J/m | ||
| ISO 180/1U | 49 kJ/m² | ||
| ISO 180/1A | 14 kJ/m² | ||
| 23°C,TotalEnergy | ASTM D3763 | 19.6 J |