Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 6345L4 CELANESE USA
FORTRON®
Automotive Applications、Electrical applications
Glass fiber reinforced、High temperature resistan、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | CELANESE USA/6345L4 |
|---|---|---|---|
| Wear factor | C-1018Steel:93°C | ASTM D3702 | 415 10^-10in³·min/ft·lb·hr |
| coefficient of friction | Dynamic3 | ASTM D1894 | 0.28 |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 150 Mpa |
| Wear factor | C-1018Steel:49°C | ASTM D3702 | 120 10^-10in³·min/ft·lb·hr |
| coefficient of friction | 与钢-动态4 | ASTM D1894 | 0.15 |
| Static3 | ASTM D1894 | 0.30 | |
| Static2 | ASTM D1894 | 0.29 | |
| bending strength | 23°C | ISO 178 | 230 Mpa |
| Flexural modulus | 23°C | ISO 178 | 10600 Mpa |
| coefficient of friction | Dynamic2 | ASTM D1894 | 0.28 |
| Wear factor | 416Stainless:32°C | ASTM D3702 | 148 10^-10in³·min/ft·lb·hr |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.9 % |
| coefficient of friction | 与钢-静态4 | ASTM D1894 | 0.17 |
| physical property | Test Condition | Test Method | CELANESE USA/6345L4 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.60-0.90 % |
| MD | ISO 294-4 | 0.30-0.50 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.020 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/6345L4 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C |
| 8.0MPa,未退火，HDT | ISO 75-2/C | 190 °C |