Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 101L DUPONT SINGAPORE
Zytel®
Industrial machinery、Household goods、Consumer goods sector
Processability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT SINGAPORE/101L |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| -30°C | ISO 179/1eA | 4.5 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 400 kJ/m² |
| 23°C | ISO 179/1eU | 无断裂 |
| hardness | Test Condition | Test Method | DUPONT SINGAPORE/101L |
|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 79 |
| R 计秤 | ISO 2039-2 | 121 |
| film | Test Condition | Test Method | DUPONT SINGAPORE/101L |
|---|---|---|---|
| Elongation - MD | 屈服 | ISO 527-3 | 4.5 % |
| Mechanical properties | Test Condition | Test Method | DUPONT SINGAPORE/101L |
|---|---|---|---|
| Tensile creep modulus | 1000 hr | ISO 899-1 | -- Mpa |
| Tensile modulus | ISO 527-2 | 3100 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 25 % | |
| Tensile stress | 屈服 | ISO 527-2 | 82.0 Mpa |
| Flexural modulus | ISO 178 | 2800 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.5 % |
| Tensile creep modulus | 1 hr | ISO 899-1 | -- Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT SINGAPORE/101L |
|---|---|---|---|
| Dissipation Factor | 1 MHz | IEC 62631-2-1 | 0.018 |
| CTI | IEC 60112 | 600 V | |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| 100 Hz | IEC 62631-2-1 | 3.80 | |
| Dissipation Factor | 100 Hz | IEC 62631-2-1 | 8.0E-3 |
| Volume resistivity | IEC 62631-3-1 | 1.0E+12 ohms·m | |
| 1 MHz | IEC 62631-2-1 | 3.50 | |
| Surface Resistivity | IEC 62631-3-2 | -- ohms |
| flammability | Test Condition | Test Method | DUPONT SINGAPORE/101L |
|---|---|---|---|
| atomization | F-value (refraction) | ISO 6452 | 99 % |
| FMVSS flammability | FMVSS 302 | DNI | |
| UL flame retardant rating | 1.5 mm | UL 94, IEC 60695-11-10, -20 | V-2 |
| 0.70 mm | UL 94, IEC 60695-11-10, -20 | V-2 | |
| Limiting Oxygen Index | ISO 4589-2 | 28 % | |
| atomization | G-value (condensate) | ISO 6452 | 1.0E-4 g |
| Filling analysis | Test Condition | Test Method | DUPONT SINGAPORE/101L |
|---|---|---|---|
| Ejection Temperature | 190 °C | ||
| Thermal Conductivity of Melt | 0.16 W/m/K | ||
| Melt density | 0.970 g/cm³ | ||
| Emission of Organic Compounds | VDA 277 | 5.00 µgC/g | |
| Odor | VDA 270 | 3.00 | |
| Specific Heat Capacity of Melt | 2790 J/kg/°C |
| physical property | Test Condition | Test Method | DUPONT SINGAPORE/101L |
|---|---|---|---|
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 8.5 % |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.6 % | |
| viscosity number | 96% H2SO4 | ISO 307 | 150 cm³/g |
| density | ISO 1183 | 1.14 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 1.4 % |
| 横向流量 | ISO 294-4 | 1.4 % |
| Thermal performance | Test Condition | Test Method | DUPONT SINGAPORE/101L |
|---|---|---|---|
| 0.45 MPa, 未退火 | ISO 75-2/B | 190 °C | |
| 流动 | ISO 11359-2 | 1.0E-4 cm/cm/°C | |
| 横向 | ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| vicat | ISO 306/B50 | 240 °C | |
| Glass transition temperature 3 | ISO 11357-2 | 60.0 °C | |
| Melting temperature 3 | ISO 11357-3 | 262 °C | |
| Effective Thermal Diffusivity | 5.00E-8 m²/s | ||
| 1.8 MPa, 未退火 | ISO 75-2/A | 70.0 °C |
| injection | Test Condition | Test Method | DUPONT SINGAPORE/101L |
|---|---|---|---|
| pressure holding | 50.0 到 100 Mpa | ||
| Maximum Screw Tangential Speed | 24 m/min | ||
| Suggested maximum moisture content | 0.20 % | ||
| Drying time - hot air dryer | 2.0 到 4.0 hr | ||
| Processing (melt) temperature | 280 到 300 °C | ||
| drying temperature | 80 °C | ||
| Temperature | 50 到 90 °C | ||
| Melt Temperature, Optimum | 290 °C | ||
| Hold Pressure Time | 4.00 s/mm | ||
| Mold Temperature, Optimum | 70 °C | ||
| pressure holding | Drying Recommended | yes |