Certificates
POM M90-44 WK3068 DAICEL MALAYSIA
--
Automotive sector
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DAICEL MALAYSIA/M90-44 WK3068 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6.0 kJ/m² |
| hardness | Test Condition | Test Method | DAICEL MALAYSIA/M90-44 WK3068 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 80 |
| Supplementary Information | Test Condition | Test Method | DAICEL MALAYSIA/M90-44 WK3068 |
|---|---|---|---|
| ColorNumber | CF2001/CD3068 |
| Mechanical properties | Test Condition | Test Method | DAICEL MALAYSIA/M90-44 WK3068 |
|---|---|---|---|
| coefficient of friction | 与钢-动态4 | JISK7218 | 0.40 |
| Wear factor | 0.060MPa,0.15m/sec7 | JISK7218 | 3500 10^-8mm³/N·m |
| Tensile modulus | ISO 527-2 | 2700 Mpa | |
| Wear factor | 0.98MPa,0.30m/sec5 | JISK7218 | <1.0 10^-8mm³/N·m |
| coefficient of friction | 与钢-动态3 | JISK7218 | 0.46 |
| Wear factor | 0.060MPa,0.15m/sec8 | JISK7218 | 6500 10^-8mm³/N·m |
| 0.49MPa,0.30m/sec5 | JISK7218 | <1.0 10^-8mm³/N·m | |
| 0.49MPa,0.30m/sec6 | JISK7218 | 65 10^-8mm³/N·m | |
| tensile strength | ISO 527-2 | 62.0 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 35 % | |
| bending strength | ISO 178 | 87.0 Mpa | |
| Flexural modulus | ISO 178 | 2500 Mpa | |
| coefficient of friction | Dynamic2 | JISK7218 | 0.37 |
| Wear factor | 0.98MPa,0.30m/sec6 | JISK7218 | 30 10^-8mm³/N·m |
| Electrical performance | Test Condition | Test Method | DAICEL MALAYSIA/M90-44 WK3068 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 19 KV/mm |
| Surface Resistivity | IEC 60093 | 1E+16 ohms |
| flammability | Test Condition | Test Method | DAICEL MALAYSIA/M90-44 WK3068 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | DAICEL MALAYSIA/M90-44 WK3068 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 2.0 % |
| melt mass-flow rate | ISO 1133 | 9.0 g/10min | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.50 % |
| density | ISO 1183 | 1.41 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 9.0 g/10min | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 2.0 % |
| Thermal performance | Test Condition | Test Method | DAICEL MALAYSIA/M90-44 WK3068 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 1.2E-04 cm/cm/°C |
| MD：23到55°C | 内部方法 | 1.2E-04 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C |