Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM FL2010-E9000 MITSUBISHI ENGINEERING JAPAN
Iupital™
Fitness equipment
wear resistant、enhance、filling
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2010-E9000 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.E+16 Ω | |
| arc resistance | ASTM D495/IEC 60112 | 600 | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.E+12 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2010-E9000 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 77 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2400 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 2650 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 18 % |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2010-E9000 |
|---|---|---|---|
| characteristic | 高耐磨级 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2010-E9000 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 2.0 % | |
| density | ASTM D792/ISO 1183 | 1.46 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.19 % |
| processability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2010-E9000 |
|---|---|---|---|
| process temperature | 180-210 °C | ||
| Dry conditions | 热风干燥 80℃---约3-4小时 | ||
| screw speed | 80-120 rpm | ||
| Temperature | 60-80 °C |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2010-E9000 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.1E-04 mm/mm.℃ |