Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6T GV-5 FWA BK 9225 EMS-CHEMIE TAIWAN
Grivory®
household electrical appl
Glass fiber reinforced、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EMS-CHEMIE TAIWAN/GV-5 FWA BK 9225 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| -30°C | ISO 179/1eU | 80 kJ/m² |
| hardness | Test Condition | Test Method | EMS-CHEMIE TAIWAN/GV-5 FWA BK 9225 |
|---|---|---|---|
| ISO 2039-1 | 280 Mpa |
| Mechanical properties | Test Condition | Test Method | EMS-CHEMIE TAIWAN/GV-5 FWA BK 9225 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 18000 Mpa | |
| Tensile stress | 断裂 | ISO 527-2 | 250 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.5 % |
| Electrical performance | Test Condition | Test Method | EMS-CHEMIE TAIWAN/GV-5 FWA BK 9225 |
|---|---|---|---|
| CTI | IEC 60112 | -- V | |
| dielectric strength | IEC 60243-1 | 33 KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+14 ohms·cm | |
| Surface Resistivity | IEC 60093 | -- ohms |
| flammability | Test Condition | Test Method | EMS-CHEMIE TAIWAN/GV-5 FWA BK 9225 |
|---|---|---|---|
| ISO Type | ISO 1874 | PA66+PA6I/X, MH, 14-190, GF50 | |
| Flammability level | 0.8 mm | IEC 60695-11-10, -20 | HB |
| physical property | Test Condition | Test Method | EMS-CHEMIE TAIWAN/GV-5 FWA BK 9225 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.4 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.10 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 4.0 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 0.40 % |
| Thermal performance | Test Condition | Test Method | EMS-CHEMIE TAIWAN/GV-5 FWA BK 9225 |
|---|---|---|---|
| 流动 | ISO 11359-2 | 1.5E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 9.0E-5 cm/cm/°C | |
| Melting temperature 5 | ISO 11357-3 | 260 °C | |
| 8.0 MPa, 未退火 | ISO 75-2/C | 165 °C | |
| Continuous use temperature | -- 3 | ISO 2578 | 100 到 120 °C |
| -- 4 | 内部方法 | 220 °C | |
| 1.8 MPa, 未退火 | ISO 75-2/A | 235 °C |