Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 CM1026 TORAY JAPAN
Amilan®
Automotive sector
Thermal stability、Medium viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | 无断裂 -- | |
| -40°C | 无断裂 -- |
| hardness | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 119 | |
| R计秤,80°C | 80 -- |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Water absorption rate | 23℃，24小时 | ASTM D-570 | 3.5%水｜- % |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -40℃，无缺口1/2 | ASTM D-256 | 3.5%水｜- kg.cm/cm |
| Flexural modulus | -40°C | MPa | 3800 3600 |
| bending strength | 23°C | MPa | 110 40.0 |
| 80°C | MPa | 40.0 25.0 | |
| Taber abraser | 1000Cycles | mg | 3.00to4.00 -- |
| tensile strength | 23°C | MPa | 80.0 35.0 |
| bending strength | 23℃ | ASTM D-790 | 3.5%水｜400 kg/cm2 |
| tensile strength | 23℃，屈服 | ASTM D-638 | 3.5%水｜350 kg/cm2 |
| Rockwell hardness | ASTM D785 | 80 | |
| 23℃ | ASTM D-785 | 无水｜119 R-标度 | |
| Flexural modulus | 80℃ | ASTM D-790 | 3.5%水｜3000 kg/cm2 |
| compressive strength | 23℃ | ASTM D-695 | 3.5%水｜650 kg/cm2 |
| tensile strength | 80°C | MPa | 25.0 20.0 |
| Tensile strain | 断裂,23°C | % | 50 |
| shear strength | 23°C | MPa | 70.0 65.0 |
| Impact strength of cantilever beam gap | 23℃，无缺口1/8 | 3.5%水｜- kg·cm/cm2 | |
| bending strength | -40°C | 135 MPa | |
| Impact strength of cantilever beam gap | 23℃，无缺口1/8 | ASTM D-256 | 3.5%水｜<50 kg.cm/cm |
| bending strength | -40℃ | ASTM D-790 | 3.5%水｜1300 kg/cm2 |
| Flexural modulus | -40℃ | ASTM D-790 | 3.5%水｜37000 kg/cm2 |
| bending strength | 80℃ | ASTM D-790 | 3.5%水｜250 kg/cm2 |
| compression stress | 23°C | MPa | 80.0 -- |
| Flexural modulus | 23℃ | ASTM D-790 | 3.5%水｜8000 kg/cm2 |
| tensile strength | 80℃，屈服 | ASTM D-638 | 3.5%水｜200 kg/cm2 |
| Flexural modulus | 23°C | 2600 MPa | |
| tensile strength | -40°C | 110 MPa | |
| Tensile strain | 屈服,23°C | % | 1.5 -- |
| elongation at break | 23℃ | ASTM D-638 | 3.5%水｜<200 % |
| shearing strength | 23℃ | ASTM D-792 | 无水｜720 kg/cm2 |
| tensile strength | -40℃，屈服 | ASTM D-638 | 3.5%水｜1000 kg/cm2 |
| Flexural modulus | 80°C | MPa | 700 300 |
| tensile strength | 23℃，断裂 | ASTM D-638 | 3.5%水｜520 kg/cm2 |
| Rockwell hardness | 80℃ | ASTM D-785 | 3.5%水｜- R-标度 |
| Friction coefficient - vs. Metal | 0.15to0.20 -- |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Volume resistivity | ASTM D-257 | 3.5%水｜1011-1012 Ω.cm | |
| ohms·cm | 1.0E+13-1.0E+14 1.0E+11到1.0E+12 | ||
| ASTM D257/IEC 60093 | 10^11-12 Ω.cm |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.13 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.8 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| UL flame retardant rating | HB -- |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | % | 11 -- |
| Shrinkage rate | MD：1.00mm3 | % | 0.40-0.90 -- |
| MD：3.00mm4 | % | 0.80-1.6 -- | |
| Taber abraser | 1000g,CS-17 | ASTM D-1044 | 3.5%水｜- mg/1000次 |
| Water absorption rate | 23°C,24hr | % | 1.8 -- |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM1026 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 182 -- |
| Linear coefficient of thermal expansion | ASTM D-696 | 3.5%水｜- ×10-5cm/cm/℃ | |
| thermal conductivity | 3.5%水｜- Kcal/m·hr·℃ | ||
| melting temperature | °C | 225 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 8E-05 -- |
| melting temperature | 差示扫描测热计DSC | 225 °C | |
| specific heat | 3.5%水｜- Cal/g·℃ | ||
| UL-94 flame retardant grade | UL 94 | 3.5%水｜- | |
| specific heat | J/kg/°C | 1900 -- | |
| thermal conductivity | W/m/K | 0.25 -- | |
| melting temperature | 225 ℃（℉） | ||
| Heat distortion temperature | 4.6kg/cm2，HDT | ASTM D-648 | 3.5%水｜- °C |