PA66 CM3004G-15 NA TORAY JAPAN
Amilan®
Electrical field、Electronic field、Automotive sector、Electrical appliances、Bottle cap、sporting goods
Flame retardant、Halogenation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM3004G-15 NA |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃ | D256 | 50 kJ/m² |
| wear resistance | D1044 | 25 mg/1000 | |
| Impact strength of cantilever beam gap | 23℃ | D256 | 80 J/m |
| tensile strength | 屈服,23℃ | D638 | 130 Mpa |
| elongation at break | 23℃ | D638 | 5 % |
| Flexural modulus | 23℃ | D790 | 7.0 GPa |
| bending strength | 23℃ | D790 | 210 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM3004G-15 NA |
|---|---|---|---|
| dielectric strength | D149 | 31 MV/m | |
| Volume resistivity | D257 | 1013 Ω.m |
| processability | Test Condition | Test Method | TORAY JAPAN/CM3004G-15 NA |
|---|---|---|---|
| Shrinkage rate | 3mmt | 0.8-1.2 % | |
| 1mmt | 0.4-0.6 % |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM3004G-15 NA |
|---|---|---|---|
| Water absorption rate | 23℃,水中 | D570 | 4.5 % |
| filler content | 20 wt% | ||
| Rockwell hardness | 23℃ | D785 | 150 R |
| Water absorption rate | 23℃,24hrs | D570 | 0.4 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM3004G-15 NA |
|---|---|---|---|
| melting temperature | DSC | 265 °C | |
| UL flame retardant rating | UL 94 | V-0 |