HMW-HDPE L5008 HMC Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | HMC Polymers/ L5008 | |
|---|---|---|---|
| density | ASTM D1505 | 0.949 g/cm³ | |
| tensile strength | 断裂 | ASTM D638 | 34.3 MPa |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 68.0 °C |
| tensile strength | 屈服 | ASTM D638 | 24.4 MPa |
| elongation | 断裂 | ASTM D638 | 640 % |
| Flexural modulus | ASTM D790 | 972 MPa | |
| Fundamentals of Hydrostatic Design | 60°C | ASTM D2837 | 6.89 MPa |
| DSCInduction Temperature | ASTM D3350 | 267 °C | |
| Slow Crack Growth (PENT) | 80°C | ASTMF1473 | >100 hr |
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 16 g/10min |
| 190°C/2.16kg | ASTM D1238 | 0.070 g/10min | |
| Fundamentals of Hydrostatic Design | 23°C | ASTM D2837 | 11.0 MPa |