PA66 22HSP BK BASF KOREA
TECHNYL®
Industrial applications,Electrical applications,Automotive Applications,Industrial machinery,Fitness equipment,Laptop case,Bushing,Shell,Cam,bearing
Chemical resistance,High rigidity,wear resistant,Oil resistant,high strength,Thermal stability,High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF KOREA/22HSP BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| Mechanical properties | Test Condition | Test Method | BASF KOREA/22HSP BK |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 95.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 85.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 5.0 % |
| Flexural modulus | 23°C | ISO 178 | 2900 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 3100 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 55.0 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 25 % |
| Poisson's ratio | ISO 527 | 0.40 |
| Electrical performance | Test Condition | Test Method | BASF KOREA/22HSP BK |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 0.71mm | UL 746 | PLC 4 |
| arc resistance | 3.00mm | ASTM D495 | PLC6 |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 4 |
| High arc combustion index (HAI) | 0.71mm | UL 746 | PLC 0 |
| 1.5mm | UL 746 | PLC 0 | |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | V |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 4 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | BASF KOREA/22HSP BK |
|---|---|---|---|
| Burning wire flammability index | 0.71mm | IEC 60695-2-12 | 825 °C |
| 3.0mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 0.71mm | IEC 60695-2-13 | 700 °C |
| UL flame retardant rating | 3.0mm | UL 94 | V-2 |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 825 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 700 °C |
| 1.5mm | IEC 60695-2-13 | 700 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| Limiting Oxygen Index | ISO 4589-2 | 24 % | |
| UL flame retardant rating | 0.71mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | BASF KOREA/22HSP BK |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 1.2 % |
| Shrinkage rate | MD:23°C,2.00mm | ISO 294-4 | 2.2 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.4 % |
| Shrinkage rate | TD:23°C,2.00mm | ISO 294-4 | 2.0 % |
| Thermal performance | Test Condition | Test Method | BASF KOREA/22HSP BK |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 1E-04 cm/cm/°C |
| RTI Imp | 1.5mm | UL 746 | 110 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 1E-04 cm/cm/°C |
| RTI Elec | 0.71mm | UL 746 | 140 °C |
| 3.0mm | UL 746 | 140 °C | |
| RTI Imp | 3.0mm | UL 746 | 110 °C |
| melting temperature | ISO 11357-3 | 260 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 200 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C | |
| RTI Str | 1.5mm | UL 746 | 125 °C |
| 3.0mm | UL 746 | 125 °C | |
| RTI Elec | 1.5mm | UL 746 | 140 °C |
| RTI Imp | 0.71mm | UL 746 | 95.0 °C |
| RTI Str | 0.71mm | UL 746 | 115 °C |