PC Kingfa JH710 G10 Kingfa
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Kingfa/Kingfa JH710 G10 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 120 J/m |
| -30°C,3.20mm | ASTM D256 | 110 J/m |
| hardness | Test Condition | Test Method | Kingfa/Kingfa JH710 G10 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 84 |
| Electrical performance | Test Condition | Test Method | Kingfa/Kingfa JH710 G10 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 19 kV/mm | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms |
| Mechanical properties | Test Condition | Test Method | Kingfa/Kingfa JH710 G10 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 9.0 % |
| tensile strength | ASTM D638 | 75.0 MPa | |
| Flexural modulus | ASTM D790 | 4200 MPa | |
| bending strength | ASTM D790 | 105 MPa |
| flammability | Test Condition | Test Method | Kingfa/Kingfa JH710 G10 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Kingfa/Kingfa JH710 G10 |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ASTM D955 | 0.30to0.40 % |
| density | ASTM D792 | 1.26 g/cm³ |
| Thermal performance | Test Condition | Test Method | Kingfa/Kingfa JH710 G10 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 130 °C |
| 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 142 °C |