PC Iupilon® EFT3200H Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® EFT3200H
Charpy Notched Impact Strength23°CISO 17965 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® EFT3200H
Nominal tensile fracture strainISO 527-2100 %
Tensile modulusISO 527-22300 MPa
Tensile strain屈服ISO 527-26.5 %
tensile strength 屈服ISO 527-262.0 MPa
Flexural modulusISO 1782300 MPa
bending strengthISO 17893.0 MPa
Electrical performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® EFT3200H
Volume resistivityIEC 600933E+16 ohms·cm
Surface ResistivityIEC 600936E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 3
flammabilityTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® EFT3200H
UL flame retardant rating2.0mmUL 94V-0
physical property Test ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® EFT3200H
Shrinkage rateTD:3.20mm0.50to0.70 %
吸水率(饱和,23°C)0.24 %
Melt volume flow rate300°C/1.2kgISO 113311.0 cm³/10min
Shrinkage rateMD:3.20mm0.50to0.70 %
densityISO 11831.20 g/cm³
melt mass-flow rate300°C/1.2kgISO 113312 g/10min
Thermal performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® EFT3200H
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B135 °C
1.8MPa,未退火，HDTISO 75-2/A122 °C
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C
TDISO 11359-26.6E-05 cm/cm/°C