PBT PRL TPSF-FRG10 Polymer Resources Ltd.
--
Structural foam
Filler, glass fiber reinforced material, 10%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Polymer Resources Ltd./PRL TPSF-FRG10 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 53 J/m |
| Mechanical properties | Test Condition | Test Method | Polymer Resources Ltd./PRL TPSF-FRG10 |
|---|---|---|---|
| Flexural modulus | 3.17mm | ASTM D790 | 2900 MPa |
| tensile strength | 屈服,3.17mm | ASTM D638 | 68.9 MPa |
| Break,3.18mm | ASTM D638 | 68.9 MPa | |
| bending strength | 3.18mm | ASTM D790 | 102 MPa |
| Electrical performance | Test Condition | Test Method | Polymer Resources Ltd./PRL TPSF-FRG10 |
|---|---|---|---|
| Hot wire ignition (HWI) | 5.4to6.6mm | UL 746 | PLC 1 |
| High arc combustion index (HAI) | 5.4to6.6mm | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | Polymer Resources Ltd./PRL TPSF-FRG10 |
|---|---|---|---|
| UL flame retardant rating | 5.4-6.6mm | UL 94 | V-05VA |
| physical property | Test Condition | Test Method | Polymer Resources Ltd./PRL TPSF-FRG10 |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 8.0to18 g/10min |
| density | ASTM D792 | 1.27 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.40to0.60 % |
| Thermal performance | Test Condition | Test Method | Polymer Resources Ltd./PRL TPSF-FRG10 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 138 °C |
| RTI Imp | 5.4to6.6mm | UL 746 | 75.0 °C |
| RTI Elec | 5.4to6.6mm | UL 746 | 75.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 121 °C |
| RTI Str | 5.4to6.6mm | UL 746 | 75.0 °C |