PA66 D.AKV15H1.0 ENVALIOR WUXI
Durethan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ENVALIOR WUXI/D.AKV15H1.0 |
|---|---|---|---|
| -30°C | ISO180/1U | 60 kJ/m² | |
| 23°C | ISO180/1U | 70 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 75 kJ/m² |
| -30°C | ISO179/1eU | 65 kJ/m² |
| Supplementary Information | Test Condition | Test Method | ENVALIOR WUXI/D.AKV15H1.0 |
|---|---|---|---|
| ISO Shortcut | ISO1874 | PA66,GHWR,14-090,GF30 |
| Electrical performance | Test Condition | Test Method | ENVALIOR WUXI/D.AKV15H1.0 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+15 ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+15 ohms·cm |
| 23°C,100Hz | IEC60250 | 4.00 | |
| 23°C,1MHz | IEC60250 | 3.60 | |
| CTI | 解决方案A | IEC60112 | 450 V |
| dielectric strength | 23°C,1.00mm | IEC60243-1 | 35 KV/mm |
| Dissipation Factor | 23°C,100Hz | IEC60250 | 8E-03 |
| 23°C,1MHz | IEC60250 | 0.016 |
| Mechanical properties | Test Condition | Test Method | ENVALIOR WUXI/D.AKV15H1.0 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO178/A | 8400 Mpa |
| Bending stress | 3.5%Strain,23°C | ISO178/A | 255 Mpa |
| 23°C4 | ISO178/A | 260 Mpa | |
| 23°C | ISO178/A | 4.5 % | |
| Tensile strain | 断裂,23°C | ISO527-2/5 | 4.0 % |
| Tensile stress | 断裂,23°C | ISO527-2/5 | 180 Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 9500 Mpa |
| flammability | Test Condition | Test Method | ENVALIOR WUXI/D.AKV15H1.0 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 650 °C |
| UL flame retardant rating | 3.2mm | UL94 | HB |
| Extreme Oxygen Index 7 | ISO4589-2 | 25 % | |
| BurningBehavior8 | ISO3795 | passed | |
| UL flame retardant rating | 1.6mm | UL94 | HB |
| physical property | Test Condition | Test Method | ENVALIOR WUXI/D.AKV15H1.0 |
|---|---|---|---|
| Shrinkage rate | MD:120°C,4hr,3.00mm3 | ISO2577 | 0.040 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 2.0 % |
| 饱和,23°C | ISO62 | 5.5 % | |
| Shrinkage rate | TD:280°C,3.00mm2 | ISO2577 | 1.3 % |
| TD:120°C,4hr,3.00mm3 | ISO2577 | 0.070 % | |
| MD:290°C,3.00mm2 | ISO2577 | 0.35 % | |
| Apparent density | ISO60 | 0.70 g/cm³ |
| Thermal performance | Test Condition | Test Method | ENVALIOR WUXI/D.AKV15H1.0 |
|---|---|---|---|
| 0.45MPa,未退火 | ISO75-2/B | 250 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 245 °C | |
| 8.0MPa,未退火 | ISO75-2/C | 125 °C | |
| Melting temperature 5 | ISO11357-3 | 262 °C | |
| vicat | ISO306/B120 | >230 °C | |
| TD：23to55°C | ISO11359-2 | 9E-05 cm/cm/°C | |
| MD：23到55°C | ISO11359-2 | 3E-05 cm/cm/°C |