PBT 2300GV1/30 CELANESE USA
CELANEX®
Electronic and electrical accessories,Automotive sector
High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | CELANESE USA/2300GV1/30 |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
-30°C | ISO 179/1eU | 60 kJ/m² |
Electrical performance | Test Condition | Test Method | CELANESE USA/2300GV1/30 |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
dielectric strength | IEC 60243-1 | 33 KV/mm | |
Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
relative permittivity | 100Hz | IEC 60250 | 4.40 |
Dissipation Factor | 100Hz | IEC 60250 | 2E-03 |
relative permittivity | 1MHz | IEC 60250 | 4.30 |
Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
Dissipation Factor | 1MHz | IEC 60250 | 0.019 |
Mechanical properties | Test Condition | Test Method | CELANESE USA/2300GV1/30 |
---|---|---|---|
Tensile creep modulus | 1hr | ISO 899-1 | 9200 Mpa |
Tensile modulus | ISO 527-2/1A/1 | 10300 Mpa | |
bending strength | 23°C | ISO 178 | 210 Mpa |
Tensile creep modulus | 1000hr | ISO 899-1 | 6500 Mpa |
tensile strength | 断裂 | ISO 527-2/1A/5 | 150 Mpa |
Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.5 % |
flammability | Test Condition | Test Method | CELANESE USA/2300GV1/30 |
---|---|---|---|
UL flame retardant rating | 1.2mm | UL 94 | HB |
1.5mm | UL 94 | HB | |
Limiting Oxygen Index | ISO 4589-2 | 20 % |
physical property | Test Condition | Test Method | CELANESE USA/2300GV1/30 |
---|---|---|---|
Shrinkage rate | TD | ISO 294-4 | 1.0-1.2 % |
SpecificHeatCapacity of Melt | 内部方法 | 1720 J/kg/°C | |
Shrinkage rate | MD | ISO 294-4 | 0.30-0.40 % |
DensityMelt | 内部方法 | 1.320 g/cm³ | |
ThermalConductivityofMelt | 内部方法 | 0.17 W/m/K | |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 9.00 cm3/10min |
Thermal performance | Test Condition | Test Method | CELANESE USA/2300GV1/30 |
---|---|---|---|
melting temperature | ISO 11357-3 | 225 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 225 °C |
vicat | ISO 306/B50 | 220 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 210 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.5E-05 cm/cm/°C |
Heat distortion temperature | 8.0MPa,未退火,HDT | ISO 75-2/C | 150 °C |