PC Iupilon® LSH2020 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LSH2020 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 12 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LSH2020 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LSH2020 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 100 % | |
| Tensile modulus | ISO 527-2 | 2500 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 6.6 % |
| tensile strength | 屈服 | ISO 527-2 | 53.0 MPa |
| Flexural modulus | ISO 178 | 2300 MPa | |
| bending strength | ISO 178 | 85.0 MPa |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LSH2020 |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LSH2020 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.50to0.70 % | |
| 吸水率(饱和,23°C) | 0.12 % | ||
| MD:3.20mm | 0.50to0.70 % | ||
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.30 cm³/10min |
| density | ISO 1183 | 1.26 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LSH2020 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 142 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 126 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.6E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7E-05 cm/cm/°C |