PA66 A218GV33 BK SOLVAY SHANGHAI
--
Application in the automo
Filler: Glass fiber reinf、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY SHANGHAI/A218GV33 BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| Electrical performance | Test Condition | Test Method | SOLVAY SHANGHAI/A218GV33 BK |
|---|---|---|---|
| relative permittivity | IEC 60250 | 3.70 | |
| Dissipation Factor | IEC 60250 | 0.010 | |
| Volume resistivity | IEC 60093 | 5E+16 ohms·cm | |
| dielectric strength | 2.00mm | IEC 60243-1 | 34 KV/mm |
| Surface Resistivity | IEC 60093 | 6E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 1 |
| Mechanical properties | Test Condition | Test Method | SOLVAY SHANGHAI/A218GV33 BK |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1A | 11300 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.4 % |
| bending strength | 23°C | ISO 178 | 300 Mpa |
| Flexural modulus | 23°C | ISO 178 | 10000 Mpa |
| bending strength | 23°C | ASTM D790 | 280 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/1A | 195 Mpa |
| 断裂,23°C | ASTM D638 | 190 Mpa | |
| Flexural modulus | 23°C | ASTM D790 | 10200 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 3.5 % |
| flammability | Test Condition | Test Method | SOLVAY SHANGHAI/A218GV33 BK |
|---|---|---|---|
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 700 °C |
| Limiting Oxygen Index | ISO 4589-2 | 23 % | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SOLVAY SHANGHAI/A218GV33 BK |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.78 % |
| 平衡,23°C,50%RH | ISO 62 | 1.7 % | |
| 饱和,23°C | ISO 62 | 5.3 % |
| Thermal performance | Test Condition | Test Method | SOLVAY SHANGHAI/A218GV33 BK |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 255 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/Af | 250 °C | |
| melting temperature | ISO 11357-3 | 262 °C |