Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS XP-2130A Samsung Cheil South Korea
INFINO® 
Automotive Applications、Laptop case
enhance、Flame retardant、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSamsung Cheil South Korea/XP-2130A
Charpy Notched Impact Strength23°CISO 179/1eA11 kJ/m²
Impact strength of cantilever beam gap23°C,6.35mmASTM D25679 J/m
23°CISO 180/1A11 kJ/m²
23°C,3.18mmASTM D25688 J/m
hardnessTest ConditionTest MethodSamsung Cheil South Korea/XP-2130A
Rockwell hardnessR级ISO 2039-2116
R级ASTM D785120
Mechanical propertiesTest ConditionTest MethodSamsung Cheil South Korea/XP-2130A
tensile strength 屈服ISO 527-2/5128 Mpa
Tensile modulusASTM D6385900 Mpa
tensile strength 断裂ISO 527-2/5115 Mpa
elongation断裂ASTM D6383.0 %
bending strengthISO 178190 Mpa
Flexural modulusISO 17810000 Mpa
bending strengthASTM D790200 Mpa
Tensile strain断裂ISO 527-2/53.0 %
Tensile modulusISO 527-2/58000 Mpa
tensile strength 断裂ASTM D638130 Mpa
屈服ASTM D638140 Mpa
Flexural modulusASTM D7909800 Mpa
flammabilityTest ConditionTest MethodSamsung Cheil South Korea/XP-2130A
UL flame retardant rating0.75mmUL 94V-0
physical property Test ConditionTest MethodSamsung Cheil South Korea/XP-2130A
ash content--ASTM D563030 %
melt mass-flow rate315°C/5.0kgASTM D1238120 g/10min
Shrinkage rateMD:3.20mmASTM D9550.30-1.2 %
TD:3.20mmISO 25770.30-1.2 %
ash content--ISO 345130 %
Shrinkage rateTD:3.20mmASTM D9550.30-1.2 %
densityASTM D7921.65 g/cm³
ISO 11831.65 g/cm³
melt mass-flow rate315°C/5.0kgISO 1133120 g/10min
Shrinkage rateMD:3.20mmISO 25770.30-1.2 %
Thermal performanceTest ConditionTest MethodSamsung Cheil South Korea/XP-2130A
Heat distortion temperature1.8MPa,Unannealed,4.00mm,HDTISO 75-2/A275 °C
1.8MPa,未退火,6.40mm,HDTASTM D648275 °C
0.45MPa,Unannealed,4.00mm,HDTISO 75-2/B289 °C
0.45MPa,未退火,6.40mm,HDTASTM D648282 °C