Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HP2REU-1H9D036T SABIC INNOVATIVE NETHERLANDS
LEXAN™
medical care、medicine、Medical/nursing supplies、medical treatment、Nursing supplies、medicine
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/HP2REU-1H9D036T |
|---|---|---|---|
| -30°C11 | ISO179/1eA | 10 kJ/m² | |
| 23°C | ASTMD256 | 70 J/m | |
| 23°C12 | ISO179/1eA | 65 kJ/m² | |
| The impact strength of a simply supported beam without a notch is 13 | 23°C | ISO179/1eU | 无断裂 |
| Unscented Izod Impact Strength 16 | -30°C | ISO180/1U | 无断裂 |
| The impact strength of a simply supported beam without a notch is 13 | -30°C | ISO179/1eU | 无断裂 |
| -30°C14 | ISO180/1A | 10 kJ/m² | |
| 23°C15 | ISO180/1A | 60 kJ/m² | |
| -30°C | ASTMD256 | 30 J/m | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 633 J |
| Unscented Izod Impact Strength 16 | 23°C | ISO180/1U | 无断裂 |
| 23°C | ISO179/2C | 35 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/HP2REU-1H9D036T |
|---|---|---|---|
| --2 | ASTMD638 | 630 Mpa | |
| yield | ISO527-2/50 | 63.0 Mpa | |
| Fracture 4 | ASTMD638 | 700 Mpa | |
| 50.0mm span 7 | ASTMD790 | 2350 Mpa | |
| Fracture 6 | ASTMD638 | 130 % | |
| fracture | ISO527-2/50 | 100 % | |
| ISO527-2/50 | 65.0 Mpa | ||
| --9 | ISO178 | 90.0 Mpa | |
| ASTMD638 | 7.0 % | ||
| Surrender 3 | ASTMD638 | 630 Mpa | |
| yield | ISO527-2/50 | 6.0 % | |
| Yield, 50.0mm span of 10 | ASTMD790 | 980 Mpa | |
| --8 | ISO178 | 2300 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/HP2REU-1H9D036T |
|---|---|---|---|
| transmissivity | 2540µm | ASTMD1003 | 88.0 % |
| Haze ratio | 2540µm | ASTMD1003 | <0.80 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/HP2REU-1H9D036T |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50到0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| 饱和,23°C | ISO62 | 0.35 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 22 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 21.0 cm3/10min |
| Shrinkage rate | MD：--1 | 内部方法 | 0.50到0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/HP2REU-1H9D036T |
|---|---|---|---|
| Flow: -40 to 40 ° C | ASTME831 | 6.8E-05 cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 6.8E-05 cm/cm/°C | |
| 0.45MPa, Unanealed, 100mm span 17 | ISO75-2/Be | 133 °C | |
| Horizontal: -40 to 40 ° C | ISO11359-2 | 7E-05 cm/cm/°C | |
| Flow: 23 to 80 ° C | ISO11359-2 | 7E-05 cm/cm/°C | |
| 1.8MPa, Unanealed, 3.20mm | ASTMD648 | 129 °C | |
| 1.8MPa, Unanealed, 100mm span 18 | ISO75-2/Ae | 122 °C |