PA66 103HSL BKB009 DUPONT USA
Zytel®
Automotive sector、Electronic field
Flame retardant、heat-resisting、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DUPONT USA/103HSL BKB009 |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1E-04 cm/cm/°C |
| Glass Transition Temperature | ISO11357-2 | 60.0 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 200 °C |
| 1.8MPa,未退火 | ISO75-2/A | 70.0 °C | |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Melting Temperature | ISO11357-3 | 262 °C | |
| Effective Thermal Diffusivity | 5E-08 m²/s | ||
| Vicat Softening Temperature | ISO306/B50 | 240 °C |
| Films Properties | Test Condition | Test Method | DUPONT USA/103HSL BKB009 |
|---|---|---|---|
| Tensile Strain (MD) | Yield | ISO527-3 | 4.5 % |
| Additional | Test Condition | Test Method | DUPONT USA/103HSL BKB009 |
|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 2.10 µgC/g | |
| Odor | VDA270 | 2.50 |
| Physical | Test Condition | Test Method | DUPONT USA/103HSL BKB009 |
|---|---|---|---|
| Viscosity number | ISO307 | 145 cm³/g | |
| Density / Specific Gravity | ISO1183 | 1.14 g/cm³ | |
| SpecificHeatCapacityofMelt | 2790 J/kg/°C | ||
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 2.6 % |
| 饱和,23°C,2.00mm | ISO62 | 8.5 % | |
| ThermalConductivityofMelt | 0.16 W/m/K | ||
| MediumDensity | 0.980 g/cm³ | ||
| Modeling Shrinkage | TD | ISO294-4 | 1.3 % |
| Ejection Temperature | 190 °C | ||
| Modeling Shrinkage | MD | ISO294-4 | 1.3 % |
| Mechanical Properties | Test Condition | Test Method | DUPONT USA/103HSL BKB009 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2800 Mpa | |
| Tensile Creep Modulus | 1000hr | ISO899-1 | -- Mpa |
| Tensile Strain | 屈服 | ISO527-2 | 4.5 % |
| Tensile Stress | 屈服 | ISO527-2 | 85.0 Mpa |
| Nominal Tensile Strain at Break | ISO527-2 | 20 % | |
| Tensile Modulus | ISO527-2 | 3100 Mpa | |
| Tensile Creep Modulus | 1hr | ISO899-1 | -- Mpa |
| Impact Properties | Test Condition | Test Method | DUPONT USA/103HSL BKB009 |
|---|---|---|---|
| Notched Izod impact strength | 23°C | ISO180/1U | NoBreak |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 6.0 kJ/m² |
| -40°C | ISO180/1A | 5.5 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.5 kJ/m² |
| 23°C | ISO179/1eA | 5.5 kJ/m² | |
| Notched Izod impact strength | -30°C | ISO180/1U | 300kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 400kJ/m² |
| 23°C | ISO179/1eU | NoBreak | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 5.0 kJ/m² |
| Flammability | Test Condition | Test Method | DUPONT USA/103HSL BKB009 |
|---|---|---|---|
| Flame Rating | 1.5mm | IEC60695-11-10,-20 | V-2 |
| 0.71mm | IEC60695-11-10,-20 | V-2 | |
| 0.71mm | UL94 | V-2 | |
| 1.5mm | UL94 | V-2 | |
| Oxygen Index | ISO4589-2 | 28 % | |
| FMVSS Flammability | FMVSS302 | SE |
| Electrical Properties | Test Condition | Test Method | DUPONT USA/103HSL BKB009 |
|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 3.80 |
| Dielectric Strength | IEC60243-1 | 31 KV/mm | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.017 |
| Volume Resistivity | IEC60093 | 1E+15 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 600 V | |
| 3.00mm | UL746 | PLC 0 | |
| Relative Permittivity | 1MHz | IEC60250 | 3.50 |
| Dissipation Factor? | 100Hz | IEC60250 | 7.5E-03 |