Certificates
PC/ABS CP8320-100 SABIC INNOVATIVE US
CYCOLAC™
Electrical applications、Automotive interior parts、Application in the automo
High mobility、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CP8320-100 |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 92.0 °C | |
| Thermal Conductivity | ISO8302 | 0.20 W/m/K | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831,ISO11359-2 | 9E-05 cm/cm/°C |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 90.0 °C | |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831,ISO11359-2 | 9E-05 cm/cm/°C |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CP8320-100 |
|---|---|---|---|
| ASTMD638 | 2100 Mpa | ||
| Break | ASTMD638 | 40.0 Mpa | |
| fracture | ISO527-2/50 | 100 % | |
| Break | ASTMD638 | 100 % | |
| Yield,50.0mm Span | ASTMD790 | 70.0 Mpa | |
| yield | ISO527-2/50 | 4.0 % | |
| Yield | ASTMD638 | 4.0 % | |
| 50.0mm Span | ASTMD790 | 2000 Mpa | |
| fracture | ISO527-2/50 | 40.0 Mpa | |
| ISO178 | 65.0 Mpa | ||
| Yield | ASTMD638 | 45.0 Mpa | |
| yield | ISO527-2/50 | 45.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/CP8320-100 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.10 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50到0.70 % |
| Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 13.0 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.30 % |
| Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 14 g/10min |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CP8320-100 |
|---|---|---|---|
| ASTMD256 | 600 J/m | ||
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂无断裂 |
| ISO180/1A | 6060 kJ/m² | ||
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 无断裂无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3030 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 55.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 6060 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂无断裂 |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 无断裂无断裂 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CP8320-100 |
|---|---|---|---|
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| 1.60mm,在油中 | IEC60243-1 | 25 KV/mm | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dielectric Strength | 0.800mm,在油中 | IEC60243-1 | 35 KV/mm |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms |