HDPE MarFlex® 9656 USA Chevron Phillips
--
Bag, mixing, lining, stretch wrapping, film
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | USA Chevron Phillips/MarFlex® 9656 |
|---|---|---|---|
| Elmendorf tear strength | TD:25.4µm | ASTM D1922 | 231.7 kN/m |
| elongation | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 500 % |
| Water Vapor Transmission Rate | 25µm,吹塑薄膜 | ASTMF1249 | 4.8 g/m²/24hr |
| Secant modulus | 1%正割,MD:25µm,吹塑薄膜 | ASTM D882 | 841 MPa |
| tensile strength | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 18.0 MPa |
| elongation | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 580 % |
| OTr | 25µm,吹塑薄膜 | ASTM D3985 | 2300 cm³/m²/24hr |
| Elmendorf tear strength | MD:25.4µm | ASTM D1922 | 5.0 kN/m |
| Dart impact | 25.4µm，吹膜 | ASTM D1709 | 19.3 kN/m |
| Secant modulus | 1%正割,TD:25µm,吹塑薄膜 | ASTM D882 | 1070 MPa |
| tensile strength | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 51.0 MPa |
| Mechanical properties | Test Condition | Test Method | USA Chevron Phillips/MarFlex® 9656 |
|---|---|---|---|
| coefficient of friction | 吹塑薄膜 | ASTM D1894 | 0.25 |
| physical property | Test Condition | Test Method | USA Chevron Phillips/MarFlex® 9656 |
|---|---|---|---|
| density | ASTM D1505 | 0.956 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.75 g/10min |