Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC FR6005 013617 COVESTRO SHANGHAI
Makrolon®
Electronic and electrical enclosure
Good appearance,Impact improvement,Easy to demould
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR6005 013617 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 垂直, 23~55℃ | ISO 11359 | 0.000070 cm/cm/°C |
| vicat | 50°C/hr50N | ISO 306 | 142 °C |
| Heat Deflection Temperature | 1.8MPa，HDT | ISO 75 | 121 °C |
| Linear coefficient of thermal expansion | 流动方向, 23~55℃ | ISO 11359 | 0.000070 cm/cm/°C |
| vicat | 120°C/hr50N | ISO 306 | 144 °C |
| Ball indentation test | ISO 11359-2 | 134 °C | |
| Heat Deflection Temperature | 0.45MPa，HDT | ISO 75 | 136 °C |
| flame retardant performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR6005 013617 |
|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| Relative temperature of heating wire | 3.0mm | ISO 11359-2 | 960 °C |
| Glow wire ignition temperature (GWIT) | 1.5mm | ISO 11359-2 | 850 °C |
| Relative temperature of heating wire | 1.0mm | ISO 11359-2 | 850 °C |
| Glow wire ignition temperature (GWIT) | 1.0mm | ISO 11359-2 | 875 °C |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 0.75mm | UL 94 | V-2 | |
| Glow wire ignition temperature (GWIT) | 3.0mm | ISO 11359-2 | 900 °C |
| Relative temperature of heating wire | 1.5mm | ISO 11359-2 | 960 °C |
| UL flame retardant rating | 1.2mm | UL 94 | V-1 |
| Mechanical properties | Test Condition | Test Method | COVESTRO SHANGHAI/FR6005 013617 |
|---|---|---|---|
| Tensile modulus | 0mm/min | ISO 527 | 2300 Mpa |
| flexural modulus | 2.0mm/min | ISO 178 | 2400 Mpa |
| Maximum puncture resistance -30 ° C | ISO 6603 | 6100 N | |
| Maximum puncture resistance at 23 ° C | ISO 6603 | 5100 N | |
| Elongation at break | 50mm/min | ISO 527 | 135 % |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 15 kJ/m² |
| tensile strength | 屈服,50mm/min | ISO 527 | 62 Mpa |
| Impact strength of cantilever beam gap | 23°C | ISO 179 | 20 kJ/m² |
| bending strength | 2.0mm/min | ISO 178 | 90 Mpa |
| Puncture Resistance | -30℃ | ISO 6603 | 55 J |
| tensile strength | 断裂50mm/min | ISO 527 | 66 Mpa |
| elongation | 屈服,50mm/min | ISO 527 | 6 % |
| Puncture Resistance | 23℃ | ISO 6603 | 54 J |
| Electrical performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR6005 013617 |
|---|---|---|---|
| volume resistivity | IEC 60093 | 90000000000000000 Ω.m | |
| CTI solution A | IEC 60112 | 200 V | |
| Surface Resistivity | IEC 60093 | 400000000000000000 Ω |
| Physical properties | Test Condition | Test Method | COVESTRO SHANGHAI/FR6005 013617 |
|---|---|---|---|
| shrinkage rate | ISO 2577 | 0.6-0.8 % | |
| melt mass-flow rate | 300°C1.2kg | ISO 1133 | 9 cm3/10min |
| density | ISO 1183 | 1200 kg/m3 | |
| shrinkage rate | 流动 | ISO 2577 | 0.6-0.8 % |