Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MABS 2802TR HD BASF GERMANY
Terlux®
Electrical appliances、Electrical field、Electronic field
Chemical resistance、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
MABS/BASF GERMANY/2802TR HD
density
ISO 1183
kg/m
Melt mass flow rate
ASTM D1238/ISO 1133
g/10min
1
Shrinkage rate
ASTM D955
%
0
Water absorption rate
equilibrium in water at 23°C
%
0.7
s
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
MABS/BASF GERMANY/2802TR HD
Charpy notch impact strength
+23℃
ISO 179/1eA
KJ/m
Charpy notch impact strength
-30℃
ISO 179/1eA
KJ/m
2
Fracture strain
50mm/min
ISO 527-1/-2
%
Impact strength of simply supported beam without notch
+23℃
ISO 179/1eU
KJ/m
Impact strength of simply supported beam without notch
-30℃
ISO 179/1eU
KJ/m
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
2
Tensile modulus
ISO 527-1/-2
Mpa
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
4
ball indentation hardness
ISO 2039-1
Mpa
Yield strain
50mm/min
ISO 527-1/-2
%
Yield stress
50mm/min
ISO 527-1/-2
Mpa
4
Impact strength of cantilever beam gap
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Impact strength of cantilever beam gap
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
8
Impact strength of cantilever beam gap
+23℃
ASTM D-256
J/m
Thermal performance
Test Condition
Test Method
Unit
MABS/BASF GERMANY/2802TR HD
Hot deformation temperature
1.80MPa
ISO 75-1/-2
℃
Hot deformation temperature
0.45MPa
ISO 75-1/-2
℃
9
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
9
vicat softening point
ASTM D1525/ISO R306
℃（℉）
1
vicat softening point
VST/A/50
ISO 306
℃
1
vicat softening point
VST/B/50
ISO 306
℃
9
Electrical performance
Test Condition
Test Method
Unit
MABS/BASF GERMANY/2802TR HD
Surface resistivity
100V
Ohm
1E+15
I
Dielectric strength
kV/mm
34
I
Dielectric loss factor
100Hz
E-4
160
I
Dielectric loss factor
1MHz
E-4
140
I
Contact Us