PPO V0150B-701 SABIC INNOVATIVE NETHERLANDS
NORYL™
Electrical applications、electrical equipment
High mobility、Chemical resistance、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/V0150B-701 |
|---|---|---|---|
| Impact strength of simply supported beam gap 8 | 23°C | ISO179/1eA | 14 kJ/m² |
| -30°C | ISO179/1eA | 5.0 kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 50.0 J |
| Suspended wall beam gap impact strength 9 | 23°C | ISO180/1A | 13 kJ/m² |
| -30°C | ISO180/1A | 5.0 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/V0150B-701 |
|---|---|---|---|
| H358/30 | ISO2039-1 | 113 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/V0150B-701 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 70.0 Mpa |
| elongation | 断裂 | ASTMD638 | 7.0 % |
| Bending modulus 6 | ISO178 | 2400 Mpa | |
| Flexural Strength5 | Yield,50.0mmSpan | ASTMD790 | 105 Mpa |
| Tensile strength 4 | Break | ASTMD638 | 60.0 Mpa |
| Tensile strain | 屈服 | ISO527-2/50 | 4.0 % |
| Tensile modulus 3 | ASTMD638 | 2500 Mpa | |
| Tensile stress | 断裂 | ISO527-2/50 | 55.0 Mpa |
| elongation | 屈服 | ASTMD638 | 5.0 % |
| Tensile modulus | ISO527-2/1 | 2500 Mpa | |
| 1000Cycles,1000g,CS-17转轮 | 内部方法 | 35.0 mg | |
| Bending strength 6,7 | ISO178 | 110 Mpa | |
| Tensile strain | 断裂 | ISO527-2/50 | 10 % |
| Flexural modulus | 50.0mmSpan | ASTMD790 | 2550 Mpa |
| Tensile strength 4 | 屈服 | ASTMD638 | 70.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/V0150B-701 |
|---|---|---|---|
| 50Hz | IEC60250 | 2.80 | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| CTI | IEC60112 | 250 V | |
| dielectric strength | 3.20mm,在油中 | IEC60243-1 | 16 KV/mm |
| Volume resistivity | IEC60093 | 1E+15 ohms·cm | |
| dielectric strength | 1.60mm,在油中 | IEC60243-1 | 26 KV/mm |
| Dissipation Factor | 60Hz | IEC60250 | 9E-04 |
| 50Hz | IEC60250 | 9E-04 | |
| 1MHz | IEC60250 | 3E-03 | |
| dielectric strength | 0.800mm,在油中 | IEC60243-1 | 33 KV/mm |
| 60Hz | IEC60250 | 2.80 | |
| 1MHz | IEC60250 | 2.70 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/V0150B-701 |
|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 775 °C |
| UL flame retardant rating | 2.0mm | UL94 | 5VA |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 775 °C |
| 2.0mm | IEC60695-2-13 | 775 °C | |
| UL flame retardant rating | 1.5mm | UL94 | V-0 |
| Limiting Oxygen Index | ISO4589-2 | 32 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/V0150B-701 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt volume flow rate | 300°C/5.0kg | ISO1133 | 10.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.060 % |
| 饱和,23°C | ISO62 | 0.18 % | |
| Shrinkage rate | MD：--2 | 内部方法 | 0.50to0.70 % |
| melt mass-flow rate | 280°C/5.0kg | ASTMD1238 | 3.5 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/V0150B-701 |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 135 °C | |
| BallPressure Test | 140°C12 | IEC60695-10-2 | Pass |
| 125°C | IEC60695-10-2 | Pass | |
| vicat | -- | ISO306/A50 | 160 °C |
| TD：23to80°C | ISO11359-2 | 9E-05 cm/cm/°C | |
| vicat | -- | ISO306/B50 | 145 °C |
| RTI Imp | UL746 | 105 °C | |
| Hot deformation temperature 10 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 130 °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 140 °C | |
| RTI Str | UL746 | 115 °C | |
| MD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C | |
| RTI Elec | UL746 | 110 °C | |
| vicat | ASTMD152511 | 155 °C | |
| MD：23到80°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| vicat | -- | ISO306/B120 | 155 °C |
| thermal conductivity | ISO8302 | 0.27 W/m/K | |
| TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |