TPU 5703 LUBRIZOL USA
ESTANE®
Coating application、adhesive、Fabric、Coating
wear resistant、Flexibility at low temper
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | LUBRIZOL USA/5703 |
|---|---|---|---|
| Shore hardness | 邵氏A | ASTM D2240 | 70 |
| Supplementary Information | Test Condition | Test Method | LUBRIZOL USA/5703 |
|---|---|---|---|
| Adhesion to PET | 305.9 g/2.5cm | ||
| GradientBarTackTemperature | 91 °C | ||
| Opening Hours | ASTM D4497-94 | >5.0 min | |
| T-shaped peel strength | AluminumFoil | ASTM D1876 | 1.8 kN/m |
| MylarFilm | ASTM D1876 | 3.4 kN/m |
| Mechanical properties | Test Condition | Test Method | LUBRIZOL USA/5703 |
|---|---|---|---|
| tensile strength | -- | ASTM D638 | 31.0 Mpa |
| elongation | 断裂,0.762mm | ASTM D638 | 630 % |
| tensile strength | 100%应变 | ASTM D638 | 2.30 Mpa |
| 300%应变 | ASTM D638 | 3.80 Mpa |
| Filling analysis | Test Condition | Test Method | LUBRIZOL USA/5703 |
|---|---|---|---|
| melt viscosity | 204°C | ASTM D1084 | 92.0 Pa·s |
| Brookfield viscosity | 15%T.S.inCyclohexanone:23°C | 1.60 Pa·s | |
| 15%T.S.inMEK/Toluene:23°C | 0.250 Pa·s |
| elastomer | Test Condition | Test Method | LUBRIZOL USA/5703 |
|---|---|---|---|
| tensile strength | 100%应变 | ASTM D412 | 2.30 Mpa |
| elongation | 断裂 | ASTM D412 | 630 % |
| tensile strength | 300%应变 | ASTM D412 | 3.80 Mpa |
| 断裂 | ASTM D412 | 31.0 Mpa |
| Thermal performance | Test Condition | Test Method | LUBRIZOL USA/5703 |
|---|---|---|---|
| Glass Transition Temperature | DSC | -31.0 °C | |
| RingandBall SoftningPoint | ASTME28-92 | 179 °C | |
| Kofler Melting Temperature | ASTM D1525 | 85 °C |