Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PET A04 900 DSM HOLAND
Arnite®
--
Nucleating、Medium viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | DSM HOLAND/A04 900 |
|---|---|---|---|
| UL flame retardant rating | 1.50 mm | IEC 60695-11-10, -20 | HB |
| 0.750 mm | IEC 60695-11-10, -20 | HB |
| Basic performance | Test Condition | Test Method | DSM HOLAND/A04 900 |
|---|---|---|---|
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.20 % |
| Shrinkage rate | Across Flow | ISO 2577 | 2.0 % |
| density | ISO 1183 | 1370 kg/m³ | |
| Shrinkage rate | Flow | ISO 2577 | 1.8 % |
| Water absorption rate | Saturation | ISO 62 | 0.50 % |
| Saturation, 23°C | ISO 62 | 0.50 % | |
| Equilibrium | ISO 62 | 0.20 % |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/A04 900 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 20 kg·cm/cm(J/M)ft·lb/in | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | No Break |
| Tensile modulus | ASTM D412/ISO 527 | 2800 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D412/ISO 527 | 70 % | |
| Flexural modulus | ASTM D790/ISO 178 | 3000 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 2800 MPa | |
| tensile strength | Yield | ISO 527-2 | 80.0 MPa |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eA | 3.0 kJ/m² |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 不断 kg·cm/cm(J/M)ft·lb/in | |
| Tensile strain | Yield | ISO 527-2 | 4.0 % |
| Rockwell hardness | ASTM D785 | 107 | |
| tensile strength | ASTM D638/ISO 527 | 81 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/A04 900 |
|---|---|---|---|
| Dielectric loss | 1MHZ | IEC 60250 | 0.0021 |
| 1E+6HZ | IEC 60250 | 0.0021 | |
| relative permittivity | 100HZ | IEC 60250 | |
| Volume resistivity | IEC 60093 | ohm·cm | |
| relative permittivity | 1E+6HZ | IEC 60250 | 3.20 |
| Dielectric loss | 100HZ | IEC 60250 | |
| relative permittivity | 1MHZ | IEC 60250 | 3.20 |
| Surface Resistivity | IEC 60093 | ohms |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/A04 900 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 255 °C | |
| Heat distortion temperature | 1.8 MPa，HDT | ISO 75-2 | 80.0 °C |
| 0.45 MPa，未退火，HDT | ISO 75-2/B | 115 °C | |
| 1.8 MPa,未退火，HDT | ISO 75-2/A | 80.0 °C | |
| 0.45 MPa，HDT | ISO 75-2 | 115 °C | |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 0.000070 cm/cm/°C |
| Transverse | ISO 11359-2 | 0.000070 cm/cm/°C |