LLDPE EVALENE® LLDPE LF10181 JG Summit Petrochemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | JG Summit Petrochemical Corporation/EVALENE® LLDPE LF10181 |
|---|---|---|---|
| Inflation ratio (BUR) | 2.00to4.00 |
| film | Test Condition | Test Method | JG Summit Petrochemical Corporation/EVALENE® LLDPE LF10181 |
|---|---|---|---|
| Dart impact | 25µm,吹塑薄膜 | ASTM D1709 | 79 g |
| Elmendorf tear strength | TD:25µm,吹塑薄膜 | ASTM D1922 | 410 g |
| tensile strength | TD:屈服,25µm,吹塑薄膜 | ASTM D882 | 8.00 MPa |
| Elmendorf tear strength | MD:25µm,吹塑薄膜 | ASTM D1922 | 200 g |
| elongation | MD:屈服,25µm,吹塑薄膜 | ASTM D882 | 61 % |
| tensile strength | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 11.0 MPa |
| elongation | TD:屈服,25µm,吹塑薄膜 | ASTM D882 | 22 % |
| TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 410 % | |
| Secant modulus | 1%正割,MD:25µm,吹塑薄膜 | ASTM D882 | 167 MPa |
| film thickness | 25 µm | ||
| tensile strength | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 10.0 MPa |
| elongation | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 410 % |
| tensile strength | MD:屈服,25µm,吹塑薄膜 | ASTM D882 | 9.00 MPa |
| Secant modulus | 1%正割,TD:25µm,吹塑薄膜 | ASTM D882 | 159 MPa |
| Mechanical properties | Test Condition | Test Method | JG Summit Petrochemical Corporation/EVALENE® LLDPE LF10181 |
|---|---|---|---|
| coefficient of friction | Dynamic,吹塑薄膜 | ASTM D1894 | 0.050 |
| Static,吹塑薄膜 | ASTM D1894 | 0.070 |
| optical performance | Test Condition | Test Method | JG Summit Petrochemical Corporation/EVALENE® LLDPE LF10181 |
|---|---|---|---|
| gloss | 45°,25.0µm,吹塑薄膜 | ASTM D2457 | 84 |
| Haze ratio | 25.0µm,吹塑薄膜 | ASTM D1003 | 14 % |
| physical property | Test Condition | Test Method | JG Summit Petrochemical Corporation/EVALENE® LLDPE LF10181 |
|---|---|---|---|
| density | ASTM D1505 | 0.918 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |