PA6 212 H Chem Polymer Company
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Chem Polymer Company/212 H |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 53 J/m |
| hardness | Test Condition | Test Method | Chem Polymer Company/212 H |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| Electrical performance | Test Condition | Test Method | Chem Polymer Company/212 H |
|---|---|---|---|
| dielectric strength | 3.00mm | ASTM D149 | 14 kV/mm |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | Chem Polymer Company/212 H |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 103 MPa |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| tensile strength | 23°C | ASTM D638 | 79.3 MPa |
| Flexural modulus | 23°C | ASTM D790 | 2860 MPa |
| elongation | 断裂,23°C | ASTM D638 | 50 % |
| flammability | Test Condition | Test Method | Chem Polymer Company/212 H |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-2 |
| Limiting Oxygen Index | ASTM D2863 | 25 % |
| physical property | Test Condition | Test Method | Chem Polymer Company/212 H |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 1.4to1.8 % |
| density | ASTM D792 | 1.13 g/cm³ | |
| melt mass-flow rate | 235°C/1.0kg | ASTM D1238 | 8.0 g/10min |
| Thermal performance | Test Condition | Test Method | Chem Polymer Company/212 H |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 92.2 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 185 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 6.2E-05 cm/cm/°C |
| melting temperature | 216 °C |