ABS ABS H607AS ELIX Polymers, S. L.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodELIX Polymers, S. L./ABS H607AS
Charpy Notched Impact Strength23°CISO 179/1eA19 kJ/m²
-30°CISO 179/1eA9.0 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A9.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU130 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A19 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU90 kJ/m²
hardnessTest ConditionTest MethodELIX Polymers, S. L./ABS H607AS
ball-indentation hardnessISO 2039-1105 MPa
Electrical performanceTest ConditionTest MethodELIX Polymers, S. L./ABS H607AS
Volume resistivityIEC 600931E+16 ohms·cm
dielectric strength23°C,1.00mmIEC 60243-131 kV/mm
relative permittivity23°C,1MHzIEC 602502.90
23°C,100HzIEC 602503.00
Surface ResistivityIEC 600931E+16 ohms
Compared to the Leakage Tracking Index (CTI)解决方案AIEC 60112PLC 0
Dissipation Factor23°C,100HzIEC 602505E-03
23°C,1MHzIEC 602509E-03
Mechanical propertiesTest ConditionTest MethodELIX Polymers, S. L./ABS H607AS
tensile strength 屈服,23°CISO 527-2/5046.0 MPa
Flexural modulus23°CISO 1782400 MPa
Tensile strain屈服,23°CISO 527-2/502.5 %
断裂,23°CISO 527-2/50>15 %
Tensile modulus23°CISO 527-2/12400 MPa
bending strength23°CISO 17870.0 MPa
flammabilityTest ConditionTest MethodELIX Polymers, S. L./ABS H607AS
burning rate2.00mmISO 379550 mm/min
Burning wire flammability index2.0mmIEC 60695-2-12700 °C
UL flame retardant rating1.6mmUL 94HB
physical property Test ConditionTest MethodELIX Polymers, S. L./ABS H607AS
Melt volume flow rate220°C/10.0kgISO 113315.0 cm³/10min
Shrinkage rateTDISO 294-40.40to0.70 %
MDISO 294-40.40to0.70 %
densityISO 11831.04 g/cm³
Thermal performanceTest ConditionTest MethodELIX Polymers, S. L./ABS H607AS
Linear coefficient of thermal expansionMD:23到55°CISO 11359-28E-05 cm/cm/°C
Heat distortion temperature1.8MPa,退火,HDTISO 75-2/A96.0 °C
vicatISO 306/B50100 °C
Heat distortion temperature0.45MPa,退火,HDTISO 75-2/B101 °C