PES JF-1002 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic field、mechanical、Bearing retainer
High temperature creep re、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/JF-1002 |
---|---|---|---|
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 54 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.6 kJ/m² |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/JF-1002 |
---|---|---|---|
Tensile modulus | ISO 527-2/1 | 4420 Mpa | |
tensile strength | 断裂 | ISO 527-2/5 | 102 Mpa |
elongation | 屈服 | ASTM D638 | 4.4 % |
Tensile strain | 屈服 | ISO 527-2/5 | 4.3 % |
tensile strength | 断裂 | ASTM D638 | 102 Mpa |
Flexural modulus | 50.0mm跨距 | ASTM D790 | 4370 Mpa |
tensile strength | 屈服 | ISO 527-2/5 | 103 Mpa |
Tensile modulus | ASTM D638 | 4680 Mpa | |
elongation | 断裂 | ASTM D638 | 5.4 % |
bending strength | 屈服,50.0mm跨距 | ASTM D790 | 176 Mpa |
Flexural modulus | ISO 178 | 4060 Mpa | |
Tensile strain | 断裂 | ISO 527-2/5 | 5.0 % |
tensile strength | 屈服 | ASTM D638 | 105 Mpa |
physical property | Test Condition | Test Method | SABIC INNOVATIVE US/JF-1002 |
---|---|---|---|
Shrinkage rate | MD:24小时 | ASTM D955 | 0.40-0.60 % |
Water absorption rate | 24hr,50%RH | ASTM D570 | 0.51 % |
平衡,23°C,50%RH | ISO 62 | 0.85 % | |
Shrinkage rate | TD:24hr | ASTM D955 | 0.50-0.70 % |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/JF-1002 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan,HDT | ISO 75-2/Bf | 221 °C |
Linear coefficient of thermal expansion | MD:-30到30°C | ASTM D696 | 3.7E-05 cm/cm/°C |
TD:-30to30°C | ASTM D696 | 4.4E-05 cm/cm/°C | |
Heat distortion temperature | 0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 220 °C |
1.8MPa,未退火,64.0mm跨距,HDT | ISO 75-2/Af | 212 °C | |
1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 214 °C |