PC/PET GM-9710R BK TEIJIN JAPAN
MULTILON®
Engineering accessories、Phone case
Glass fiber reinforced、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/GM-9710R BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 70 kJ/m² |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/GM-9710R BK |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/GM-9710R BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3800 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 82.0 Mpa |
| bending strength | ISO 178 | 130 Mpa | |
| Flexural modulus | ISO 178 | 3700 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 4.0 % |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/GM-9710R BK |
|---|---|---|---|
| Melt volume flow rate | 280°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.18 % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.40-0.60 % |
| TD:4.00mm | 内部方法 | 0.50-0.70 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/GM-9710R BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 140 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 130 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7E-05 cm/cm/°C |