LLDPE Jam PE 14X01 Jam Petrochemical Company
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | Jam Petrochemical Company/Jam PE 14X01 |
|---|---|---|---|
| Inflation ratio (BUR) | 2.00to3.00 |
| film | Test Condition | Test Method | Jam Petrochemical Company/Jam PE 14X01 |
|---|---|---|---|
| Dart impact | 25µm,吹塑薄膜 | ASTM D1709 | 100 g |
| Secant modulus | 2%正割,TD:25µm,吹塑薄膜 | ASTM D882 | 215 MPa |
| Elmendorf tear strength | TD:25µm,吹塑薄膜 | ASTM D1922 | 360 g |
| tensile strength | TD:屈服,25µm,吹塑薄膜 | ASTM D882 | 12.1 MPa |
| elongation | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 890 % |
| Secant modulus | 2%正割,MD:25µm,吹塑薄膜 | ASTM D882 | 185 MPa |
| Elmendorf tear strength | MD:25µm,吹塑薄膜 | ASTM D1922 | 140 g |
| film thickness | 25 µm | ||
| tensile strength | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 40.0 MPa |
| MD:屈服,25µm,吹塑薄膜 | ASTM D882 | 13.5 MPa | |
| elongation | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 590 % |
| tensile strength | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 51.0 MPa |
| optical performance | Test Condition | Test Method | Jam Petrochemical Company/Jam PE 14X01 |
|---|---|---|---|
| gloss | 45°,25.0µm,吹塑薄膜 | ASTM D2457 | 46 |
| Haze ratio | 25.0µm,吹塑薄膜 | ASTM D1003 | 19 % |
| physical property | Test Condition | Test Method | Jam Petrochemical Company/Jam PE 14X01 |
|---|---|---|---|
| density | ASTM D1505 | 0.914 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.95 g/10min |