Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

TPV 201-87 CELANESE USA
Santoprene™
Electrical applications、Automotive Applications、household electrical appl、Home appliance components、Parts under the hood of a、Pipe fittings、Electrical components、Application in the automo、diaphragm、Movable hinge、Consumer product applicat
Chemical resistance、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | CELANESE USA/201-87 |
---|---|---|---|
Shore hardness | 邵氏A,15秒,23°C | ISO 868 | 93 |
Electrical performance | Test Condition | Test Method | CELANESE USA/201-87 |
---|---|---|---|
High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
dielectric strength | 23°C,2.00mm | ASTM D149 | 32 KV/mm |
Hot wire ignition (HWI) | 1.0mm | UL 746 | PLC 4 |
High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 3 |
3.0mm | UL 746 | PLC 2 | |
dielectric constant | 23°C,1.98mm | IEC 60250 | 2.40 |
23°C,1.98mm | ASTM D150 | 2.40 | |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
High Voltage Arc Traceability Rate (HVTR) | PLC | UL 746 |
flammability | Test Condition | Test Method | CELANESE USA/201-87 |
---|---|---|---|
UL flame retardant rating | 3.0mm | UL 94 | HB |
1.0mm | UL 94 | HB | |
1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | CELANESE USA/201-87 |
---|---|---|---|
Resistance to cleaning agents | UL 749 | f3 | |
ISO 188 | f4 |
elastomer | Test Condition | Test Method | CELANESE USA/201-87 |
---|---|---|---|
elongation | 断裂,23°C,横向 | ASTM D412 | 580 % |
Tensile stress | 100%应变,23°C,横向流量 | ISO 37 | 7.10 Mpa |
tensile strength | 断裂,23°C,横向流量 | ASTM D412 | 15.0 Mpa |
elongation | 断裂,23°C,横向 | ISO 37 | 580 % |
tear strength | 23°C,Across Flow (横向) | ISO 34-1 | 54 kN/m |
tensile strength | Break,23°C | ISO 37 | 15.0 Mpa |
compression set | 70°C,22hr | ISO 815 | 36 % |
70°C,22hr | ASTM D395B | 36 % | |
125°C,70hr | ISO 815 | 44 % | |
tear strength | 23°C,横向流量 | ASTM D624 | 54.0 kN/m |
Tensile stress | 100%应变,23°C,横向流量 | ASTM D412 | 7.10 Mpa |
compression set | 125°C,70hr | ASTM D395B | 44 % |
aging | Test Condition | Test Method | CELANESE USA/201-87 |
---|---|---|---|
Change rate of tensile strength in air | 125°C,70hr,inIRM903Oil | ASTM D471 | -29 % |
elongation at break | 125°C,70hr,inIRM903Oil | ASTM D471 | -32 % |
Tensile strain change rate | 125°C,70hr,inIRM903Oil | ISO 1817 | -29 % |
Change rate of elongation at break | 125°C,70hr,inIRM903Oil | ISO 1817 | -32 % |
volume change | 125°C,70hr,在IRM903油中 | ASTM D471 | 48 % |
Hardness change rate in the air | ShoreA,150°C,168hr | ASTM D573 | 2.0 |
Change rate of ultimate elongation in air | 150°C,168hr | ASTM D573 | -16 % |
Change rate of tensile strength in air | 150°C,168hr | ASTM D573 | -15 % |
volume change | 125°C,70hr,在IRM903油中 | ISO 1817 | 48 % |
Change rate of tensile strength in air | 150°C,168hr | ISO 188 | -15 % |
Shore hardness | ShoreA,150°C,168hr | ISO 188 | 2.0 |
Thermal performance | Test Condition | Test Method | CELANESE USA/201-87 |
---|---|---|---|
brittle temperature | ISO 812 | -54.0 °C | |
RTI Str | 1.0mm | UL 746 | 90.0 °C |
brittle temperature | ASTM D746 | -54.0 °C | |
RTI Str | 1.5mm | UL 746 | 90.0 °C |
3.0mm | UL 746 | 95.0 °C | |
RTI Elec | UL 746 | 100 °C |