PBT 430 BK SABIC INNOVATIVE US
VALOX™
Automotive External Parts、Electrical field、Electronic field、Electrical appliances、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Laptop case
Glass fiber reinforced、Impact modification、Filler: Glass fiber reinf、33% filler by weight、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/430 BK |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 130 J/m |
| 23°C | ASTM D4812 | 860 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/430 BK |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 125 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/430 BK |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 8670 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.1 % |
| tensile strength | Break | ASTM D638 | 106 Mpa |
| bending strength | Break,50.0mmSpan | ASTM D790 | 174 Mpa |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 7810 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/430 BK |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 0 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/430 BK |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/430 BK |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 12 g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50 % |
| TD：--2 | 内部方法 | 0.40-0.60 % | |
| Water absorption rate | 24hr | ASTM D570 | 0.050 % |
| Shrinkage rate | TD：--4 | 内部方法 | 0.60-0.90 % |
| MD：--2 | 内部方法 | 0.30-0.50 % | |
| density | ASTM D792 | 1.52 g/cm³ | |
| Specific volume | ASTM D792 | 0.650 cm³/g | |
| Shrinkage rate | MD：--3 | 内部方法 | 0.50-0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/430 BK |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 208 °C |
| 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 223 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 140 °C | |
| RTI Elec | UL 746 | 130 °C |