Mechanical properties	Test Condition	Test Method	KURARAY JAPAN/H171B
Tensile modulus		ISO 527-2	2600 Mpa
Charpy Notched Impact Strength		ISO 179	2.0 kJ/m²
Tensile strain	断裂	ISO 527-2	15 %
Flexural modulus		ISO 178	4800 Mpa
tensile strength	断裂	ISO 527-2	27.0 Mpa
Rockwell hardness	M 计秤	ISO 2039-2	85

physical property	Test Condition	Test Method	KURARAY JAPAN/H171B
melt mass-flow rate	190℃/2.16 kg	ISO 1133	1.7 g/10 min
Ethylene component			38.0 wt%
melt mass-flow rate	210℃/2.16 kg	ISO 1133	3.4 g/10 min

Thermal performance	Test Condition	Test Method	KURARAY JAPAN/H171B
Glass Transition Temperature	DSC	DSC	53.0 °C
Crystallization peak temperature	DSC	ISO 3146	148 °C
melting temperature		ISO 3146	172 °C