Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 DPBKV60H2.0EF 900116 LANXESS INDIA
Durethan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS INDIA/DPBKV60H2.0EF 900116 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 80 kJ/m² |
| 23°C | ISO 180/1U | 80 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| -30°C | ISO 179/1eU | 90 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LANXESS INDIA/DPBKV60H2.0EF 900116 |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA6.GHR.10-220.GF60 |
| hardness | Test Condition | Test Method | LANXESS INDIA/DPBKV60H2.0EF 900116 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 255 Mpa |
| Electrical performance | Test Condition | Test Method | LANXESS INDIA/DPBKV60H2.0EF 900116 |
|---|---|---|---|
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 33 KV/mm |
| relative permittivity | 23°C,1MHz | IEC 60250 | 4.70 |
| Volume resistivity | 23°C | IEC 60093 | 5.8E+14 ohms·cm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 5.30 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 0.016 |
| 23°C,1MHz | IEC 60250 | 0.018 |
| Mechanical properties | Test Condition | Test Method | LANXESS INDIA/DPBKV60H2.0EF 900116 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.4 % |
| Flexural modulus | 23°C | ISO 178/A | 19300 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 225 Mpa |
| Bending Strain | 23°C | ISO 178/A | 2.8 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 20000 Mpa |
| bending strength | 23°C | ISO 178/A | 365 Mpa |
| physical property | Test Condition | Test Method | LANXESS INDIA/DPBKV60H2.0EF 900116 |
|---|---|---|---|
| Shrinkage rate | MD:120°C,4小时,2.00mm3 | ISO 2577 | 0.030 % |
| TD:280°C,2.00mm2 | ISO 2577 | 0.40 % | |
| MD:280°C,2.00mm2 | ISO 2577 | 0.32 % | |
| Apparent density | ISO 60 | 0.75 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.3 % |
| 饱和,23°C | ISO 62 | 3.6 % | |
| Shrinkage rate | TD:120°C,4小时,2.00mm3 | ISO 2577 | 0.060 % |
| Thermal performance | Test Condition | Test Method | LANXESS INDIA/DPBKV60H2.0EF 900116 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 222 °C | |
| vicat | ISO 306/B120 | 210 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 1.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 213 °C |