Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS POLYblend PC/ABS 45H POLYKEMI SWEDEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYKEMI SWEDEN/POLYblend PC/ABS 45H |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 43 kJ/m² |
| -30°C | ISO 179 | 15 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| -30°C | ISO 179 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | POLYKEMI SWEDEN/POLYblend PC/ABS 45H |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 2300 MPa |
| tensile strength | ISO 527-2 | 59.0 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 7.0 % |
| bending strength | ISO 178 | 93.0 MPa |
| flammability | Test Condition | Test Method | POLYKEMI SWEDEN/POLYblend PC/ABS 45H |
|---|---|---|---|
| Hot filament ignition temperature | 3.2mm | IEC 60695-2-13 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYKEMI SWEDEN/POLYblend PC/ABS 45H |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.50to0.70 % |
| MD | ISO 294-4 | 0.50to0.70 % | |
| melt mass-flow rate | 240°C/5.0kg | ISO 1133 | 12 g/10min |
| density | ISO 1183 | 1.10 g/cm³ |
| Thermal performance | Test Condition | Test Method | POLYKEMI SWEDEN/POLYblend PC/ABS 45H |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 110 °C |
| vicat | -- | ISO 306/A50 | 124 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 100 °C |
| ball-indentation hardness | 95°C | IEC 60695-10-2 | 通过 |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 92.0 °C |
| vicat | -- | ISO 306/B50 | 107 °C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 112 °C |