TSU-Ester InnoTuf® HP-1090A Innovative Polymers, Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1090A |
|---|---|---|---|
| Taber abraser | 1000Cycles,1000g,H-18转轮 | ASTM D4060 | 15.0 mg |
| Uncured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1090A |
|---|---|---|---|
| Viscosity | 43°C3 | 0.85 Pa·s | |
| 固化时间5 | 1.8E+02 hr | ||
| 43°C2 | 0.60 Pa·s | ||
| 43°C4 | 1.5 Pa·s | ||
| GelTime | 10to16 min |
| thermosetting | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1090A |
|---|---|---|---|
| Thermosetting components | 硬化法 | 按重量计算的混合比:100按容量计算的混合比:100 | |
| 树脂 | 按重量计算的混合比:82按容量计算的混合比:77 | ||
| 脱模时间(66°C) | 60to180 min |
| Cured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1090A |
|---|---|---|---|
| tear strength | ASTM D624 | 66.5 kN/m | |
| elongation | 断裂 | ASTM D638 | 470 % |
| tensile strength | ASTM D638 | 31.0 MPa | |
| Shore hardness | ShoreA | ASTM D2240 | 85to95 |
| elastomer | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1090A |
|---|---|---|---|
| tear strength | 开裂 | ASTM D470 | 20 kN/m |
| physical property | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1090A |
|---|---|---|---|
| density | Hardener | 1.13 g/cm³ | |
| 基体树脂 | 1.20 g/cm³ | ||
| Cured | 1.16 g/cm³ | ||
| Shrinkage rate | MD | ASTM D2566 | 1.0to1.5 % |