PC PRL PC-UV2-D(f1) Polymer Resources Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-UV2-D(f1) |
|---|---|---|---|
| Dart impact | 3.18mm | ASTM D3029 | >36.2 J |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 800 J/m |
| hardness | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-UV2-D(f1) |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 70 |
| R计秤 | ASTM D785 | 118 |
| Electrical performance | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-UV2-D(f1) |
|---|---|---|---|
| dielectric strength | 0.750mm | ASTM D149 | 12 kV/mm |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | 0.750mm | UL 746 | PLC 2 |
| arc resistance | 0.750mm | ASTM D495 | PLC 5 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | 0.750mm | UL 746 | PLC 3 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-UV2-D(f1) |
|---|---|---|---|
| elongation | 断裂,3.18mm | ASTM D638 | 140 % |
| Flexural modulus | 3.17mm | ASTM D790 | 2310 MPa |
| tensile strength | 屈服,3.17mm | ASTM D638 | 62.1 MPa |
| Break,3.18mm | ASTM D638 | 68.9 MPa | |
| elongation | 屈服,3.18mm | ASTM D638 | 6.5 % |
| bending strength | 3.18mm | ASTM D790 | 95.8 MPa |
| optical performance | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-UV2-D(f1) |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| flammability | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-UV2-D(f1) |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| 3.0mm | UL 94 | V-2 | |
| 1.5mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-UV2-D(f1) |
|---|---|---|---|
| Outdoor applicability | UL 746C | f1 | |
| density | ASTM D792 | 1.20 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.50to0.70 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 9.0to16 g/10min |
| Thermal performance | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-UV2-D(f1) |
|---|---|---|---|
| RTI Imp | 0.75mm | UL 746 | 80.0 °C |
| RTI Str | 0.75mm | UL 746 | 80.0 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 135 °C |
| RTI Imp | 1.5mm | UL 746 | 105 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 129 °C |
| RTI Str | 1.5mm | UL 746 | 120 °C |
| vicat | ASTM D15252 | 152 °C | |
| RTI Str | 3.0mm | UL 746 | 120 °C |
| RTI Elec | 1.5mm | UL 746 | 120 °C |
| 3.0mm | UL 746 | 120 °C | |
| RTI Imp | 3.0mm | UL 746 | 110 °C |
| RTI Elec | 0.75mm | UL 746 | 80.0 °C |