Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 HTN52G30BL DUPONT USA
Zytel®
Automotive interior equipment,Profile,building materials
High temperature resistan,Aging resistance,Flame retardant,Filler: Glass fiber reinf,30% filler by weight,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/HTN52G30BL |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 40 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| -30°C | ISO 179/1eU | 50 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/HTN52G30BL |
|---|---|---|---|
| Odor | VDA270 | 4.50 |
| thermal performance | Test Condition | Test Method | DUPONT USA/HTN52G30BL |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 282 °C |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO 11359-2 | 5.7E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 300 °C |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 2E-05 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 2E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 1E-05 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 6.3E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| melting temperature | ISO 11357-3 | 310 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/HTN52G30BL |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 12000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 170 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| bending strength | ISO 178 | 250 Mpa | |
| flexural modulus | ISO 178 | 10500 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/HTN52G30BL |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.50 |
| Dissipation Factor | 100Hz | IEC 60250 | 5E-03 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 3.30 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| 解决方案B | IEC 60112 | PLC 3 | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.014 |
| Compared to the Leakage Tracking Index (CTI) | -- | IEC 60112 | PLC 1 |
| Physical properties | Test Condition | Test Method | DUPONT USA/HTN52G30BL |
|---|---|---|---|
| density | ISO 1183 | 1.62 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.30 % |
| flammability | Test Condition | Test Method | DUPONT USA/HTN52G30BL |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | V-0 |
| atomization | refraction，F值 | ISO 6452 | 95 % |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| FMVSS flammability | FMVSS302 | DNI | |
| Limiting Oxygen Index | ISO 4589-2 | 42 % | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |