Certificates

SPS EA533 DUPONT-DOW US
--
--
Glass fiber reinforced,Filler/fiberglass reinfor,30% weight filler
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Basic Performance | Test Condition | Test Method | DUPONT-DOW US/EA533 |
---|---|---|---|
density | ISO 1183/B | 1.39 | |
Water absorption rate | Stauration,23℃ | ISO 62 | 0.090 % |
thermal performance | Test Condition | Test Method | DUPONT-DOW US/EA533 |
---|---|---|---|
Hot deformation temperature | 1.80MPa,Unannealed | ISO 75-2/B | 245 °C |
RTI Elec | 1.50mm | UL 746 | 125 °C |
RTI Imp | 1.50mm | UL 746 | 120 °C |
RTI Str | 1.50mm | UL 746 | 120 °C |
UL flame retardant rating | 1.50mm | UL 94 | V-0 |
Vicat softening temperature | ISO 306 | 260 °C |
mechanical properties | Test Condition | Test Method | DUPONT-DOW US/EA533 |
---|---|---|---|
Bending modulus | ISO 178 | 10400 Mpa | |
bending strength | ISO 178 | 195 Mpa | |
Charpy Notched Impact Strength | ISO 179 | 9.00 kJ/m² | |
Fracture strain | ISO 527-2 | 1.9 % | |
Impact strength of cantilever beam gap | ISO 180 | 12.0 KJ/m | |
Impact strength of simply supported beam without notch | ISO 179 | 39.00 KJ/m | |
Suspended wall beam without notch impact strength | ISO 180 | 50.0 KJ/m | |
Tensile stress | Yield | ISO 527-2 | 125 Mpa |
Electrical performance | Test Condition | Test Method | DUPONT-DOW US/EA533 |
---|---|---|---|
Dielectric constant | IEC 60250 | 3.200 | |
Dielectric loss | IEC 60250 | 0.00200 | |
Volume resistivity | IEC 60093 | 1.3E+18 ohm.cm |
Physical properties | Test Condition | Test Method | DUPONT-DOW US/EA533 |
---|---|---|---|
Shrinkage rate | Flow | ISO 294-4 | 0.15-0.30 % |
Across Flow | ISO 294-4 | 0.70-0.90 % |