Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PARA 1524/9008 BK SOLVAY USA
IXEF®
Automotive interior parts、sporting goods、Shell、Phone
high strength、Creep resistance、Filler: Glass fiber reinf、50% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SOLVAY USA/1524/9008 BK |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 227 °C |
| Physical | Test Condition | Test Method | SOLVAY USA/1524/9008 BK |
|---|---|---|---|
| Modeling Shrinkage | MD | 内部方法 | 0.10to0.30 % |
| Moisture Absorption | 平衡,50%RH | 内部方法 | 1.0 % |
| Equilibrium,65%RH | 内部方法 | 1.3 % | |
| 23°C,24hr | ISO62 | 0.30 % |
| Mechanical Properties | Test Condition | Test Method | SOLVAY USA/1524/9008 BK |
|---|---|---|---|
| Flexural Modulus | ISO178 | 18500 Mpa | |
| Tensile Stress | 屈服 | ISO527-2 | 230 Mpa |
| Tensile Strain | 断裂 | ISO527-2 | 1.9 % |
| Flexural Stress | ISO178 | 330 Mpa | |
| Tensile Modulus | ISO527-2 | 20000 Mpa |
| Impact Properties | Test Condition | Test Method | SOLVAY USA/1524/9008 BK |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179/1eU | 48 kJ/m² |
| Flammability | Test Condition | Test Method | SOLVAY USA/1524/9008 BK |
|---|---|---|---|
| Glow Wire Ignition Temperature | 0.75mm | IEC60695-2-13 | 800 °C |
| 0.40mm | IEC60695-2-13 | 775 °C | |
| 3.0mm | IEC60695-2-13 | 850 °C | |
| Oxygen Index | ISO4589-2 | 37 % | |
| Flame Rating | 0.40mm,ALL | UL94 | V-0 |
| Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 825 °C |
| Electrical Properties | Test Condition | Test Method | SOLVAY USA/1524/9008 BK |
|---|---|---|---|
| Hot-wire Ignition | 1.50mm | UL746 | >120 sec |
| 3.0mm | UL746 | PLC 0 | |
| Dielectric Constant | 2.40GHz | ASTMD2520 | 4.44 |
| Hot-wire Ignition | 1.5mm | UL746 | PLC 0 |
| 0.750mm | UL746 | >120 sec | |
| Comparative Tracking Index | IEC60112 | >600 V | |
| Hot-wire Ignition | 0.40mm | UL746 | PLC 1 |
| High Amp Arc Ignition | 0.400mm | UL746 | 37.6 |
| Hot-wire Ignition | 3.00mm | UL746 | >120 sec |
| Comparative Tracking Index | 3.00mm | UL746 | PLC 0 |
| High Amp Arc Ignition | 1.50mm | UL746 | 70.2 |
| 1.5mm | UL746 | PLC 1 | |
| 3.0mm | UL746 | PLC 1 | |
| 0.75mm | UL746 | PLC 2 | |
| Hot-wire Ignition | 0.400mm | UL746 | 95 sec |
| 0.75mm | UL746 | PLC 0 | |
| Comparative Tracking Index | 3.00mm | UL746 | >600 V |
| High Amp Arc Ignition | 3.00mm | UL746 | 95.4 |
| High Voltage Arc Tracking Rate | 3.00mm | UL746 | PLC 0 |
| 2.40GHz | ASTMD2520 | 0.012 | |
| High Amp Arc Ignition | 0.40mm | UL746 | PLC 2 |
| 0.750mm | UL746 | 53.6 |