HDPE SNOLEN® IM 55/59 JSC Gazprom neftekhim Salavat
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® IM 55/59 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 2.0 kJ/m² |
| hardness | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® IM 55/59 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 64 |
| Mechanical properties | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® IM 55/59 |
|---|---|---|---|
| Tensile modulus | 23°C，正割 | ISO 527-2/1 | 1350 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 10 % |
| 断裂 | ISO 527-2/50 | >1000 % | |
| tensile strength | 屈服 | ISO 527-2/50 | 28.0 MPa |
| 断裂 | ISO 527-2/50 | 30.0 MPa |
| physical property | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® IM 55/59 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 0.955to0.959 g/cm³ |
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 49to55 g/10min |
| Melt flow ratio | 2.40to3.60 | ||
| Environmental stress cracking resistance | 80°C,2%Arkopal | ISO 16770 | 1.00 hr |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 14to20 g/10min |
| Thermal performance | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® IM 55/59 |
|---|---|---|---|
| vicat | ISO 306/B50 | 71.0 °C | |
| brittle temperature | ASTM D746 | <-80.0 °C |