PPS 1140A1 JAPAN POLYPLASTIC
DURAFIDE®
Fiber grade
High toughness、High temperature resistan、Flame retardant、Glass fiber reinforced
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A1 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 105 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A1 |
|---|---|---|---|
| ColorNumber | HF2000/HD9050 |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A1 |
|---|---|---|---|
| Dissipation Factor | 1kHz | IEC 60250 | 2E-03 |
| relative permittivity | 1kHz | IEC 60250 | 4.60 |
| Dissipation Factor | 耐电弧性 | IEC 60250 | 120 sec |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 15 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 4.60 |
| Volume resistivity | ASTM D257/IEC 60093 | 1.0 x 10^16 Ω.cm | |
| Dissipation Factor | 1MHz | IEC 60250 | 2E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A1 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 260 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 13000 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 260 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.8 % |
| Flexural modulus | ISO 178 | 1300 Mpa | |
| elongation at break | ASTM D638/ISO 527 | 1.8 % | |
| tensile strength | ASTM D638/ISO 527 | 185 kg/cm²(MPa)[Lb/in²] | |
| ISO 527-2 | 185 Mpa |
| other | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A1 |
|---|---|---|---|
| characteristic | 高韧性 | ||
| Color | 黑色/本色 | ||
| purpose | 汽车配件/电子电器 |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A1 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.66 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.01 % |
| processability | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A1 |
|---|---|---|---|
| process temperature | 310-320 °C | ||
| Dry conditions | 160℃3H | ||
| Temperature | 150 °C |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A1 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A1 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.030 % |
| melt viscosity | 310°C,1000sec^-1 | ISO 11443 | 380000 mPa·s |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A1 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Linear coefficient of thermal expansion | TD | 内部方法 | 4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 265 °C |
| Linear coefficient of thermal expansion | MD | 内部方法 | 1E-05 cm/cm/°C |
| ASTM D696/ISO 11359 | - mm/mm.℃ |