PC K-1300Y TEIJIN JAPAN
PANLITE®
transparent,Translucent accessories,film,sheet,Cleaning Compound
transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTEIJIN JAPAN/K-1300Y
Impact strength of simply supported beam without notchISO 179NoBreak
Electrical performanceTest ConditionTest MethodTEIJIN JAPAN/K-1300Y
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
Surface ResistivityASTM D257/IEC 60093>1×10 15 Ω
dielectric constant100HZIEC 602503.1
Dielectric loss100HZ，正切IEC 6025010
dielectric constantASTM D150/IEC 602503.1
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602501E-03
Dielectric loss1MHZ，正切IEC 6025090
dielectric constant1MHzIEC 602503
arc resistanceASTM D495/IEC 6011230
relative permittivity1MHzIEC 602503.00
Volume resistivityASTM D257/IEC 60093>1×10 13 Ω.cm
Dissipation Factor1MHzIEC 602509E-03
dielectric strengthIEC 60243-130 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
IEC 60093＞1×10 Ω.m
Surface ResistivityIEC 60093>1.0E+15 ohms
IEC 60093＞1×10 Ω
Mechanical propertiesTest ConditionTest MethodTEIJIN JAPAN/K-1300Y
Impact strength of cantilever beam gapASTM D256/ISO 17989 kg·cm/cm(J/M)ft·lb/in
bending strengthASTM D790/ISO 17890 kg/cm²(MPa)[Lb/in²]
Tensile modulusISO 527-2/12350 Mpa
Flexural modulusASTM D790/ISO 1782200 kg/cm²(MPa)[Lb/in²]
elongationASTM D638/ISO 5276 %
elongation at breakASTM D638/ISO 527>50 %
Tensile strain屈服ISO 527-2/506.0 %
Nominal tensile fracture strainISO 527-2/50>50 %
Tensile stressISO 527-160 Mpa
Impact strength of cantilever beam gap带缺口ISO 17989 KJ/m
tensile strength 屈服ISO 527-2/5060.0 Mpa
bending strengthISO 17890.0 Mpa
Flexural modulusISO 1782200 Mpa
Tensile modulusASTM D638/ISO 5272400 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap没缺口ISO 179NB KJ/m
elongation at yieldISO 527-16 %
Tensile modulusISO 527-12350 Mpa
elongation断裂ISO 527-1＞50 %
optical performance Test ConditionTest MethodTEIJIN JAPAN/K-1300Y
transmissivity3000µmASTM D100388.0 %
refractive indexASTM D542/ISO 4891.585
ASTM D5421.585
transmittance3mm厚ASTM D100388 %
ASTM D1003/ISO 1346888 %
Physical propertiesTest ConditionTest MethodTEIJIN JAPAN/K-1300Y
Shrinkage rateASTM D9550.5-0.7 %
densityASTM D792/ISO 11831200
Water absorption rateASTM D570/ISO 620.2 %
flammabilityTest ConditionTest MethodTEIJIN JAPAN/K-1300Y
UL flame retardant rating0.38mmUL 94HB
physical property Test ConditionTest MethodTEIJIN JAPAN/K-1300Y
Shrinkage rate0.5-0.7 %
Water absorption rate23°C,24hrISO 620.20 %
Melt volume flow rate300°C/1.2kgISO 11332.80 cm3/10min
Water absorption rate23℃,24hrsISO 620.2 %
Melt volume flow rateISO 11332.5 CM
Shrinkage rateMD:4.00mm内部方法0.50-0.70 %
TD:4.00mm内部方法0.50-0.70 %
Thermal performanceTest ConditionTest MethodTEIJIN JAPAN/K-1300Y
RTI Imp1.5mmUL 746115 °C
vicatISO 306151 °C
ISO 306/B50151 °C
Heat distortion temperature1.80MPa，HDTISO 75-1132 °C
Linear coefficient of thermal expansionASTM D696/ISO 113590.7 mm/mm.℃
ISO 11359-20.7
Heat distortion temperatureHDTASTM D648/ISO 75145 ℃（℉）
vicatASTM D1525/ISO R306151 ℃（℉）
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B145 °C
1.8MPa,未退火，HDTISO 75-2/A132 °C
RTI Str1.5mmUL 746125 °C
Linear coefficient of thermal expansionMDISO 11359-27E-05 cm/cm/°C
RTI Elec1.5mmUL 746125 °C
Linear coefficient of thermal expansionTDISO 11359-27E-05 cm/cm/°C
UL flame retardant ratingUL 94HB