PA66 ARV300RKC 106 NT RADICI SUZHOU
Radilon®
--
Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | RADICI SUZHOU/ARV300RKC 106 NT |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
-30°C | ISO 179/1eU | 75 kJ/m² |
Electrical performance | Test Condition | Test Method | RADICI SUZHOU/ARV300RKC 106 NT |
---|---|---|---|
Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
Surface Resistivity | IEC 60093 | 1E+12 ohms | |
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
Mechanical properties | Test Condition | Test Method | RADICI SUZHOU/ARV300RKC 106 NT |
---|---|---|---|
Tensile modulus | ISO 527-2/1A/1 | 9800 Mpa | |
bending strength | ISO 178 | 290 Mpa | |
Flexural modulus | ISO 178 | 8900 Mpa | |
tensile strength | 断裂 | ISO 527-2/1A/5 | 190 Mpa |
Tensile strain | 断裂 | ISO 527-2/1A/5 | 3.6 % |
flammability | Test Condition | Test Method | RADICI SUZHOU/ARV300RKC 106 NT |
---|---|---|---|
burning rate | FMVSS302 | 0.0 mm/min | |
UL flame retardant rating | 0.8mm | UL 94 | HB |
Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 700 °C |
physical property | Test Condition | Test Method | RADICI SUZHOU/ARV300RKC 106 NT |
---|---|---|---|
Shrinkage rate | TD | ISO 294-4 | 1.2 % |
MD | ISO 294-4 | 0.50 % | |
Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 6.2 % |
平衡,23°C,2.00mm,50%RH | ISO 62 | 1.6 % |
Thermal performance | Test Condition | Test Method | RADICI SUZHOU/ARV300RKC 106 NT |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 245 °C |
melting temperature | ISO 11357 | 260 °C | |
vicat | ISO 306/B50 | 250 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/Bf | 255 °C |