Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 2870-21317 SABIC INNOVATIVE US
LEXAN™
chip、food
high viscosity、Food contact compliance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| Dart impact | ASTM D 3029 | 170 J | |
| Charpy Notched Impact Strength | V-notch Edgew，23℃ | ISO 179/1eA | 70 kJ/m² |
| Suspended wall beam without notch impact strength | 80*10*3，-30℃ | ISO 180/1A | 55 kJ/m² |
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 750 J/m |
| Suspended wall beam without notch impact strength | 23℃ | ASTM D 4812 | NB J/m |
| Charpy Notched Impact Strength | V-notch Edgew，-30℃ | ISO 179/1eA | 50 kJ/m² |
| Suspended wall beam without notch impact strength | 80*10*3，23℃ | ISO 180/1A | 75 kJ/m² |
| 80*10*3，23℃ | ISO 180/1U | NB kJ/m² | |
| Impact strength of cantilever beam gap | /，30℃ | ASTM D256 | 150 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| Hardness (Rockwell R) | ISO 2039-2 | 120 R |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| elongation | 50 mm/m，屈服 | ISO 527 | 7 % |
| elongation at break | Type I, 5 | ASTM D638 | 70 % |
| Flexural modulus | 1.3 mm/min | ASTM D790 | 2300 Mpa |
| elongation at break | 50 mm/m | ISO 527 | 70 % |
| Flexural modulus | 2 mm/mi | ISO 178 | 2300 Mpa |
| tensile strength | 50 mm/m，屈服 | ISO 527 | 65 Mpa |
| elongation | Type I, 5，屈服 | ASTM D638 | 7 % |
| tensile strength | 50 mm/m，断裂 | ISO 527 | 70 Mpa |
| bending strength | 1.3 mm/min/，屈服 | ASTM D790 | 95 Mpa |
| tensile strength | Type I, 50，断裂 | ASTM D638 | 65 Mpa |
| bending strength | 2 mm/，屈服 | ISO 178 | 95 Mpa |
| tensile strength | Type I, 5，屈服 | ASTM D638 | 62 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| transmittance | 2.54 mm | ASTM D1003 | 88 % |
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| vicat | Rate B/5 | ISO 306 | 149 °C |
| specific heat | ASTM C 351 | 1.25 J/g-°C | |
| vicat | Rate B/5 | ASTM D1525 | 150 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| Melt volume flow rate | 300°C/2.16 kg | ISO 1133 | 4 cm³/10 min |
| melt mass-flow rate | / | ASTM D1238 | 2.5 g/10min |
| Water absorption rate | equilibriu | ASTM D570 | 0.35 |
| 23°C/sat | ISO 62 | 0.35 | |
| 23°C / 50 | ISO 62 | 0.15 | |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 2 cm³/10 min |
| Shrinkage rate | flow, 3. | Internal | 0.5-0.7 |