TPEE HTR8206 DUPONT USA
Hytrel®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| hardness | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 40 |
| 邵氏D,15秒 | ISO 868 | 38 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 80.0 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 420 % | |
| Flexural modulus | ISO 178 | 80.0 Mpa | |
| tensile strength | 10%应变 | ISO 527-2 | 5.40 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | >300 % |
| tensile strength | 断裂 | ISO 527-2 | 20.0 Mpa |
| 50%应变 | ISO 527-2 | 9.50 Mpa | |
| 5.0%应变 | ISO 527-2 | 3.40 Mpa |
| flammability | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.5 % |
| MD | ISO 294-4 | 1.4 % | |
| MediumDensity | 1.02 g/cm³ | ||
| Water absorption rate | 23°C,24hr | ISO 62 | 35 % |
| Melt volume flow rate | 220°C/2.16kg | ISO 1133 | 14.0 cm3/10min |
| SpecificHeatCapacity of Melt | 2100 J/kg/°C | ||
| ThermalConductivityofMelt | 0.16 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.3 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/HTR8206 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 200 °C | |
| Effective thermal diffusivity coefficient | 5.44E-08 m²/s |